SABIC Innovative Plastics LNP THERMOCOMP RF002SXS PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF002SXS PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF002SXS is a compound based on Nylon 66 resin contaning 10% Glass Fiber. Characteristcs of this grade are: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.860 % | 0.860 % | 50% RH, 24 hrs; ASTM D570 |
| 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
| 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.43 GPa | 788 ksi | 1 mm/min; ISO 527 |
| 5.44 GPa | 789 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| 147 MPa | 21300 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 144 MPa | 20900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.34 GPa | 629 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.48 GPa | 650 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.300 J/cm | 0.562 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.85 J/cm | 5.34 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 82.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
45.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 256 °C @Thickness 3.20 mm |
493 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 238 °C @Thickness 3.20 mm |
460 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer (Asia Pacific)
- SABIC Innovative Plastics Lexan® LUX2910 PC (Asia Pacific)
- Lehmann & Voss LUVOCOM® 1200-7116 ABS, with carbon fiber
- Loxim 820 02T V0 Polypropylene Compound, 20% Talc Filled, Flame Retardant
- Lanxess Pocan® BF 4232 HR 901510 PBT, 30% Glass Fiber
- BASF Ultramid® 8202 L Intermediate PA6 (Conditioned)
- BASF Pluracol® P1010 Specialty Polyol
- Ferro EG 2800 Metal Sealing
- Hexion Bakelite™ PF 2874 Phenolic Formaldehyde Resin, Low Shrinkage, Improved Electrical Properties, UL Listed, High Mechanical Strength
Copyright © lookpolymers.com All Rights Reserved