Entec Hyril® GP355AS Styrene Acrylonitrile

Category	Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Transparent
Manufacturer	Entec Engineered Resins
Trade Name	Hyril®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Entec Hyril® GP355AS Styrene Acrylonitrile.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Available in North America Features: Copolymer Automotive Specifications: DELPHI M-9565-9 Color: Blue-TransparentForm: PelletsProcessing Method: ExtrusionInformation provided by Entec

Physical Properties	Metric	English	Comments
Specific Gravity	1.07 g/cc	1.07 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0030 - 0.0070 cm/cm	0.0030 - 0.0070 in/in	ASTM D955
Melt Flow	8.0 g/10 min @Load 3.80 kg, Temperature 230 °C	8.0 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	125	125	ASTM D785
Tensile Strength, Yield	71.7 MPa	10400 psi	ASTM D638
Elongation at Break	2.5 %	2.5 %	ASTM D638
Flexural Yield Strength	123 MPa	17900 psi	ASTM D790
Flexural Modulus	3.87 GPa	561 ksi	ASTM D790
Izod Impact, Notched	0.160 J/cm	0.300 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	59.4 µm/m-°C	33.0 µin/in-°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	96.7 °C	206 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	85.6 °C	186 °F	Unannealed; ASTM D648
Vicat Softening Point	108 °C	227 °F	Rate B (120°C/h), Loading 1 (10 N); ASTM D1525

Optical Properties	Metric	English	Comments
Haze	0.60 %	0.60 %	ASTM D1003
Transmission, Visible	89 %	89 %	ASTM D1003

Processing Properties	Metric	English
Zone 1	162 - 191 °C	323 - 375 °F
Zone 3	204 - 232 °C	400 - 450 °F
Die Temperature	232 - 246 °C	450 - 475 °F
Roll Temperature	10.0 - 87.8 °C	50.0 - 190 °F
Drying Temperature	71.1 - 82.2 °C @Time 7200 - 14400 sec	160 - 180 °F @Time 2.00 - 4.00 hour
Moisture Content	<= 0.60 %	<= 0.60 %