SABIC Innovative Plastics LNP THERMOCOMP LC006 PEEK (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP LC006 PEEK (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* LC006 is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 219 MPa | 31800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 23.4 GPa | 3390 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 301 MPa | 43700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 17.0 GPa | 2470 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 6.90 µm/m-°C @Temperature 23.0 - 60.0 °C |
3.83 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 300 °C | >= 572 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 - 1.00e+6 ohm | 10000 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- MV Labs PR700 Pr(NO3)3·6H2O Praseodymium nitrate hexahydrate
- PSM Industries Ferro-TiC® MS-5A Age Hardenable Martensitic Stainless Steel
- PolyOne Stat-Tech™ PF-NX-062100-2 Polysulfone (discontinued **)
- Loxim 230 01HB Polybutylene Terephthalate
- SABIC Innovative Plastics NORYL GTX GTX4610 PPE+PA
- DuPont™ Kevlar® 49 Aramid Fiber
- Arkema Group Lacovyl® PB 1303 PVC
- Ashley Polymers Ashlene® 1061R Polycarbonate
- DuPont Teijin Films Melinex® 454 Polyester Film, 300 Gauge
Copyright © lookpolymers.com All Rights Reserved