MRC Polymers NAXALOYâ„¢ 770-NT137 ABS + PC Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | MRC Polymers |
| Trade Name | NAXALOY™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers NAXALOYâ„¢ 770-NT137 ABS + PC Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D 792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D 570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D 785 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D 638 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D 790 |
| Flexural Modulus | 2.069 GPa | 300.1 ksi | ASTM D 790 |
| Izod Impact, Notched | 4.27 J/cm @Temperature -20.0 °C |
8.00 ft-lb/in @Temperature -4.00 °F |
ASTM D 256 |
| 6.41 J/cm @Temperature 23.0 °C |
12.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Dart Drop, Total Energy | 52.0 J @Temperature -28.9 °C |
38.4 ft-lb @Temperature -20.0 °F |
ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D 648 |
Users viewing this material also viewed the following:
- RheTech Products T20P252-01 20% Talc Reinforced Polypropylene Copolymer, Black
- Ravago Manufacturing Americas Hylon® N2033THL Nylon 6 (DAM)
- LTL Color Compounds ColorRxâ„¢ ABS-0505ARX Biocompatible, Antimicrobial ABS
- Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes
- SABIC Innovative Plastics LNP THERMOCOMP RF0039S PA 66
- Sapco 99.9% Aluminum Oxide
- A. Schulman POLYBATCH™ White P8555 T2 Concentrate Based In Homopolymer Polypropylene
- Polyplastics Duracon® ES-5 Acetal Co-polymer (POM), Conductive, Antistatic
- Arlon 51141R020 Silicone Rubber/Fiberglass Laminate
- Ineos H20E-00 Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved