SABIC Innovative Plastics LNP THERMOCOMP KB008 Acetal Copolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP KB008 Acetal Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* KB008 is a compound based on Acetal Copolymer resin containing 40% Glass Bead.
Physical Properties Metric English Comments
Density 1.71 g/cc
0.0618 lb/in³
ISO 1183
Water Absorption 0.30 %

@Time 86400 sec
 0.30 %

@Time 24.0 hour
 ISO 62-1
Linear Mold Shrinkage, Flow 0.022 cm/cm
0.022 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.0 MPa
5080 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 4.60 GPa
667 ksi
1 mm/min; ISO 527
Flexural Yield Strength 71.0 MPa
10300 psi
2 mm/min; ISO 178
Flexural Modulus 4.80 GPa
696 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 93.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 51.7 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 88.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 48.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 108 °C
226 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af