SABIC Innovative Plastics LNP THERMOCOMP KB006 Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP KB006 Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* KB006 is a compound based on Acetal containing 30% Glass Bead.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.64 g/cc | 1.64 g/cc | ASTM D792 |
| Density | 1.64 g/cc | 0.0592 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.040 cm/cm @Time 86400 sec |
0.010 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D638 |
| 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 19.8 % | 19.8 % | Type I, 5 mm/min; ASTM D638 |
| 20.4 % | 20.4 % | 5 mm/min; ISO 527 | |
| Flexural Strength | 43.0 MPa | 6240 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 65.0 MPa | 9430 psi | ISO 178 | |
| Flexural Modulus | 3.99 GPa | 579 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.32 GPa | 627 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Unnotched | 3.74 J/cm | 7.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 83.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 155 °C @Thickness 3.20 mm |
311 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 103 °C @Thickness 3.20 mm |
218 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Lanxess Durethan® AM 40 X H2.0 901510 Nylon 66, Glass Fiber/Mineral Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP KAL22XXC Acetal Copolymer
- Techmer ES HiFill® PA4/6 GF50 HS BK 50% Glass Filled
- A. Schulman PP 1901-01 Polypropylene High-Flow Homopolymer Polypropylene
- A. Schulman POLYFORT™ FPP 1640 Glass Reinforced, Mineral Fortified Homopolymer Polypropylene
- Eastman Tenite 550E3V45510 Cellulose Acetate Butyrate, Water Clear, Trsp
- Aclo Accutech ABS ABS831G30L Glass Reinforced
- A. Schulman PAPERMATCH® T-4448/50 Specialty Masterbatch
- Chevron Phillips K-Resin® BK11 Styrene-Butadiene Copolymer, Injection Molding Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved