SABIC Innovative Plastics LNP THERMOCOMP DX11355 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DX11355 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a PC based compound with good plating, surface, mechanical performance and flame retardant (Halogen free), a good candidate for Laser Direct Structuring applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 70 % | 70 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.4 % | 5.4 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.60 GPa | 377 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 8.00 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C @Thickness 3.20 mm |
237 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.600 mm |
V-0 @Thickness 0.0236 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.92 @Frequency 1.00e+9 Hz |
2.92 @Frequency 1.00e+9 Hz |
IEC 60250 |
| Dissipation Factor | 0.0070 @Frequency 1.00e+9 Hz |
0.0070 @Frequency 1.00e+9 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- NatureWorks® Ingeo™ 6204D Fiber Grade PLA
- PolyOne Geon™ Vinyl Flexible A8500 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Lubrizol Advanced Materials PEARLTHANE® 16N85UV Thermoplastic Polyurethane Elastomer (discontinued **)
- Solvay JAGUAR® HP 8FF Surfactant
- Hexcel® HexWeb® CR-PAA™ 1/8-5052-0.0037 Phosphoric Acid Anodized Aluminum Honeycomb
- A. Schulman POLYBATCH™ Hot Sauce Red 50323/2 Concentrate Based In LLDPE
- Adamas Adalon® 807 PTFE, 40% Bronze + 5 MoS2
- 3M FP024802 Clear Polypropylene Label Products
- Polyplastics Duracon® CH-10 Acetal Co-polymer (POM), Conductive, CF reinforced, Wear resistance
- SABIC Innovative Plastics Lexan® HFD4412 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved