AFE Technologies Cronite 37Ni/18Cr No. HR5

Category	Metal , Nonferrous Metal , Nickel Alloy , Superalloy , Iron Base
Manufacturer	AFE TEchnologies; North American Cronite
Trade Name	Cronite
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	AFE Technologies Cronite 37Ni/18Cr No. HR5.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AFE Technologies/North American Cronite, Inc.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	460 MPa	66700 psi	As Cast
Tensile Strength, Yield	240 MPa	34800 psi	As Cast
Elongation at Break	6.0 %	6.0 %	As Cast; 5.65 A<sup>0.5</sup>
Rupture Strength	3.20 MPa @Temperature 1150 °C, Time 3.60e+7 sec	464 psi @Temperature 2100 °F, Time 10000 hour	Stress Rupture
	4.70 MPa @Temperature 1100 °C, Time 3.60e+7 sec	682 psi @Temperature 2010 °F, Time 10000 hour	Stress Rupture
	7.00 MPa @Temperature 1050 °C, Time 3.60e+7 sec	1020 psi @Temperature 1920 °F, Time 10000 hour	Stress Rupture
	10.5 MPa @Temperature 1000 °C, Time 3.60e+7 sec	1520 psi @Temperature 1830 °F, Time 10000 hour	Stress Rupture
	16.0 MPa @Temperature 950 °C, Time 3.60e+7 sec	2320 psi @Temperature 1740 °F, Time 10000 hour	Stress Rupture
	23.0 MPa @Temperature 900 °C, Time 3.60e+7 sec	3340 psi @Temperature 1650 °F, Time 10000 hour	Stress Rupture
	32.0 MPa @Temperature 850 °C, Time 3.60e+7 sec	4640 psi @Temperature 1560 °F, Time 10000 hour	Stress Rupture
	42.0 MPa @Temperature 800 °C, Time 3.60e+7 sec	6090 psi @Temperature 1470 °F, Time 10000 hour	Stress Rupture
	56.0 MPa @Temperature 750 °C, Time 3.60e+7 sec	8120 psi @Temperature 1380 °F, Time 10000 hour	Stress Rupture
	75.0 MPa @Temperature 700 °C, Time 3.60e+7 sec	10900 psi @Temperature 1290 °F, Time 10000 hour	Stress Rupture

Component Elements Properties	Metric	English	Comments
Carbon, C	0.40 %	0.40 %
Chromium, Cr	18 %	18 %
Iron, Fe	41.8 %	41.8 %	As Remainder
Manganese, Mn	1.0 %	1.0 %
Nickel, Ni	37 %	37 %
Silicon, Si	1.8 %	1.8 %

Users viewing this material also viewed the following: