SABIC Innovative Plastics LNP THERMOCOMP DX06411H PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP THERMOCOMP DX06411H PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* THERMOCOMP* DX06411H is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.

Physical Properties	Metric	English	Comments
Specific Gravity	1.35 g/cc	1.35 g/cc	ASTM D792
Density	1.35 g/cc	0.0488 lb/inÂ³	ASTM D792
Moisture Absorption	0.0100 %	0.0100 %	50% RH, 24 hrs; ASTM D570
	0.0100 %	0.0100 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0030 - 0.0050 cm/cm @Time 86400 sec	0.0030 - 0.0050 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Time 86400 sec	0.0050 - 0.0070 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	101 MPa	14600 psi	Type I, 5 mm/min; ASTM D638
	102 MPa	14800 psi	5 mm/min; ISO 527
Tensile Strength, Yield	104 MPa	15100 psi	Type I, 5 mm/min; ASTM D638
	104 MPa	15100 psi	5 mm/min; ISO 527
Elongation at Break	3.8 %	3.8 %	5 mm/min; ISO 527
	3.9 %	3.9 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	2.9 %	2.9 %	5 mm/min; ISO 527
	3.1 %	3.1 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	6.96 GPa	1010 ksi	50 mm/min; ASTM D638
	6.99 GPa	1010 ksi	1 mm/min; ISO 527
Flexural Strength	174 MPa	25200 psi	1.3 mm/min, 50 mm span; ASTM D790
	175 MPa	25400 psi	ISO 178
Flexural Yield Strength	174 MPa	25200 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	6.00 GPa	870 ksi	2 mm/min; ISO 178
	6.09 GPa	883 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	1.18 J/cm	2.21 ft-lb/in	ASTM D256
Izod Impact, Unnotched	9.47 J/cm	17.7 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	11.0 kJ/mÂ²	5.23 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	59.0 kJ/mÂ²	28.1 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	18.0 J @Temperature 23.0 Â°C	13.3 ft-lb @Temperature 73.4 Â°F	ASTM D3763
Impact Test	4.00 J	2.95 ft-lb	Multiaxial Impact; ISO 6603

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	3.00 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	1.67 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
CTE, linear, Transverse to Flow	7.00 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	3.89 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	143 Â°C	289 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	140 Â°C @Thickness 3.20 mm	284 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	137 Â°C	279 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	136 Â°C @Thickness 3.20 mm	277 Â°F @Thickness 0.126 in	unannealed; ASTM D648