PolyOne Bergadur™ PB40 G15 UF UV Polybutylene Terephthalate (PBT)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergadur™ |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | PolyOne Bergadur™ PB40 G15 UF UV Polybutylene Terephthalate (PBT).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ±0.03 g/cm³; DIN 53479 |
| Melt Index of Compound | 18 g/10 min <br>@Load 1.60 kg,<br> Temperature 250 °C |
18 g/10 min <br>@Load 3.53 lb,<br> Temperature 482 °F |
cm³/10min; ISO 1133 |
| Ash | 15 % | 15 % | ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa <br>@Temperature 23.0 °C |
9430 psi <br>@Temperature 73.4 °F |
ISO 527-2/5 |
| Elongation at Break | 4.0 % <br>@Temperature 23.0 °C |
4.0 % <br>@Temperature 73.4 °F |
ISO 527-2/5 |
| Tensile Modulus | 4.60 GPa <br>@Temperature 23.0 °C |
667 ksi <br>@Temperature 73.4 °F |
ISO 527-2/1 |
| Charpy Impact Unnotched | 6.70 J/cm² <br>@Temperature 23.0 °C |
31.9 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.950 J/cm² <br>@Temperature 23.0 °C |
4.52 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 224 °C | 435 °F | ISO 3146 |
| Maximum Service Temperature, Air | 135 °C | 275 °F | Continuous (GTP 50% Tensile); IEC 60216 |
| 170 °C | 338 °F | Short Time; IEC 60216 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Unannealed; ISO 75-2/B |
| Flammability, UL94 | V-0 <br>@Thickness 1.60 mm |
V-0 <br>@Thickness 0.0630 in |
Internal Method |
| Glow Wire Test | 960 °C <br>@Thickness 3.00 mm |
1760 °F <br>@Thickness 0.118 in |
1.6 mm wire; Ignition Temperature; IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | UV Stabilizer | |
| Features | Flame Retardant | |
| Halogen Free | ||
| Low (to None) Phosphorus Content | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 15% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | PBT | |
| Generic Name | Polybutylene Terephthalate (PBT) | |
| Regional Availability | Africa & Middle East | |
| Europe | ||
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Hardwire 3x2-4-12 Low Density Composite
- Haynes 556® alloy, 50% cold reduction
- Saint-Gobain Norton® F510 General Purpose Skived PTFE Sheet
- Sax Polymers SAXATEC 6120 AES
- American Polymers API 505 HF Polystyrene
- A. Schulman LP554-01 Narrow Molecular Weight Homopolymer, High-Density Polyethylene
- Williams Advanced Alloys WS314A Solder
- Diamond Polymers DIAMALOY 530 PC/PBT Alloy, UV Stabilized/Weatherable
- BASF 2-Phenylethylamine
Copyright © lookpolymers.com All Rights Reserved