SABIC Innovative Plastics LNP THERMOCOMP DX05477 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DX05477 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DX05477 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| 1.271 g/cc | 0.04592 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0059 cm/cm @Time 86400 sec |
0.0059 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | ASTM D638 |
| 69.0 MPa | 10000 psi | ISO 527 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ASTM D638 |
| 70.0 MPa | 10200 psi | ISO 527 | |
| Elongation at Break | 4.4 % | 4.4 % | ISO 527 |
| 7.4 % | 7.4 % | ASTM D638 | |
| Elongation at Yield | 3.8 % | 3.8 % | ISO 527 |
| 4.2 % | 4.2 % | ASTM D638 | |
| Tensile Modulus | 2.82 GPa | 409 ksi | 50 mm/min; ASTM D638 |
| 3.60 GPa | 522 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 119 MPa | 17300 psi | ASTM D790 |
| 120 MPa | 17400 psi | ISO 178 | |
| Flexural Modulus | 3.44 GPa | 499 ksi | ASTM D790 |
| 3.70 GPa | 537 ksi | ISO 178 | |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Ovation Polymers OpteSTAT™ NC PPS 7010 Polyphenylenesulfide based Carbon Nanotube Compound
- Premix Premi-Glas® 3200-30 Fiberglass Reinforced SMC
- Momentive Performance Materials Siloprenâ„¢ LSR 2760 Liquid Silicone Rubber - Self-Bonding
- Samsung Cheil Industries Infino® HR-8070 MPPE, Unreinforced
- A. Schulman POLYBATCH™ Brown 10305U Concentrate Based In LLDPE
- ExxonMobil Exxsol™ Methylpentane Naphtha Dearomatized Fluid
- Arlon 55833R062 Mar Resistant Press Pad; 1.6 mm Cured Silicone Rubber with Fiberglass Substrate
- AK Steel Cold Rolled Carbon Steel, Commercial Steel (CS Type B), Standard Grade
- Pau Tai Avanstab BT-404 Organotin Stabilizer Butyl Thiotin
Copyright © lookpolymers.com All Rights Reserved