Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed

Category Metal , Nonferrous Metal , Nickel Alloy
Manufacturer Haynes International, Inc.
Trade Name Hastelloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing species. The alloy also exhibits extremely high resistance to pitting and crevice corrosion. HYBRID-BC1 alloy is available in the form of plate, sheet, strip, billet, bar, wire, pipe, and tube. HYBRID-BC1 alloy is suitable for the following applications in the chemical processing, pharmaceutical, agricultural, food, petrochemical, and power industries: Reaction vessels Heat exchangers Valves Pumps Piping Storage tanks The alloy is suitable for use at temperatures up to approximately 427°C (800°F). HYBRID-BC1 alloy excels in reducing acids and acid mixtures (with or without halides) open to oxygen and other oxidizing residuals/contaminants. Heat Treatment: Wrought forms of HYBRID-BC1 alloy are furnished in the solution annealed condition, unless otherwise specified. The standard solution annealing treatment consists of heating to 1149°C (2100°F) followed by rapid air-cooling or (preferably) water quenching. Parts which have been hot formed should be solution annealed prior to final fabrication or installation. The minimum hot forming temperature of the alloy is 954°C (1750°F). Forming: HYBRID-BC1 alloy has excellent forming characteristics, and cold forming is the preferred method of shaping. The alloy can be easily cold worked due to its high ductility; however, the alloy is stronger than the austenitic stainless steels and therefore requires more energy during cold forming.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.83 g/cc
0.319 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 683 MPa

@Thickness 19.1 mm,
Temperature 427 °C
 99100 psi

@Thickness 0.752 in,
Temperature 801 °F
688 MPa

@Thickness 19.1 mm,
Temperature 371 °C
 99800 psi

@Thickness 0.752 in,
Temperature 700 °F
692 MPa

@Thickness 19.1 mm,
Temperature 316 °C
 100000 psi

@Thickness 0.752 in,
Temperature 601 °F
706 MPa

@Thickness 19.1 mm,
Temperature 260 °C
 102000 psi

@Thickness 0.752 in,
Temperature 500 °F
723 MPa

@Thickness 19.1 mm,
Temperature 204 °C
 105000 psi

@Thickness 0.752 in,
Temperature 399 °F
749 MPa

@Thickness 19.1 mm,
Temperature 149 °C
 109000 psi

@Thickness 0.752 in,
Temperature 300 °F
778 MPa

@Thickness 19.1 mm,
Temperature 93.0 °C
 113000 psi

@Thickness 0.752 in,
Temperature 199 °F
809 MPa

@Thickness 19.1 mm,
Temperature 25.0 °C
 117000 psi

@Thickness 0.752 in,
Temperature 77.0 °F
Tensile Strength, Yield 225 MPa

@Thickness 19.1 mm,
Temperature 427 °C
 32600 psi

@Thickness 0.752 in,
Temperature 801 °F
 0.2% Offset
240 MPa

@Thickness 19.1 mm,
Temperature 371 °C
 34800 psi

@Thickness 0.752 in,
Temperature 700 °F
 0.2% Offset
245 MPa

@Thickness 19.1 mm,
Temperature 316 °C
 35500 psi

@Thickness 0.752 in,
Temperature 601 °F
 0.2% Offset
246 MPa

@Thickness 19.1 mm,
Temperature 260 °C
 35700 psi

@Thickness 0.752 in,
Temperature 500 °F
 0.2% Offset
268 MPa

@Thickness 19.1 mm,
Temperature 204 °C
 38900 psi

@Thickness 0.752 in,
Temperature 399 °F
 0.2% Offset
294 MPa

@Thickness 19.1 mm,
Temperature 149 °C
 42600 psi

@Thickness 0.752 in,
Temperature 300 °F
 0.2% Offset
327 MPa

@Thickness 19.1 mm,
Temperature 93.0 °C
 47400 psi

@Thickness 0.752 in,
Temperature 199 °F
 0.2% Offset
362 MPa

@Thickness 19.1 mm,
Temperature 25.0 °C
 52500 psi

@Thickness 0.752 in,
Temperature 77.0 °F
 0.2% Offset
Elongation at Break 70.5 %

@Thickness 19.1 mm,
Temperature 25.0 °C
 70.5 %

@Thickness 0.752 in,
Temperature 77.0 °F
71.1 %

@Thickness 19.1 mm,
Temperature 316 °C
 71.1 %

@Thickness 0.752 in,
Temperature 601 °F
74 %

@Thickness 19.1 mm,
Temperature 371 °C
 74 %

@Thickness 0.752 in,
Temperature 700 °F
74.6 %

@Thickness 19.1 mm,
Temperature 204 °C
 74.6 %

@Thickness 0.752 in,
Temperature 399 °F
74.7 %

@Thickness 19.1 mm,
Temperature 260 °C
 74.7 %

@Thickness 0.752 in,
Temperature 500 °F
74.8 %

@Thickness 19.1 mm,
Temperature 93.0 °C
 74.8 %

@Thickness 0.752 in,
Temperature 199 °F
74.8 %

@Thickness 19.1 mm,
Temperature 149 °C
 74.8 %

@Thickness 0.752 in,
Temperature 300 °F
76.3 %

@Thickness 19.1 mm,
Temperature 427 °C
 76.3 %

@Thickness 0.752 in,
Temperature 801 °F
Modulus of Elasticity 188 GPa

@Temperature 600 °C
 27300 ksi

@Temperature 1110 °F
 Dynamic
191 GPa

@Temperature 500 °C
 27700 ksi

@Temperature 932 °F
 Dynamic
197 GPa

@Temperature 400 °C
 28600 ksi

@Temperature 752 °F
 Dynamic
200 GPa

@Temperature 300 °C
 29000 ksi

@Temperature 572 °F
 Dynamic
205 GPa

@Temperature 200 °C
 29700 ksi

@Temperature 392 °F
 Dynamic
211 GPa

@Temperature 100 °C
 30600 ksi

@Temperature 212 °F
 Dynamic
217 GPa

@Temperature 25.0 °C
 31500 ksi

@Temperature 77.0 °F
 Dynamic
Charpy Impact 347 J

@Temperature -196 °C
 256 ft-lb

@Temperature -321 °F
 Notched, Solution Annealed + 2000 h at 427°C
>= 358 J

@Temperature 25.0 °C
 >= 264 ft-lb

@Temperature 77.0 °F
 Notched, Solution Annealed + 2000 h at 427°C
>= 358 J

@Temperature 25.0 °C
 >= 264 ft-lb

@Temperature 77.0 °F
 Notched
>= 358 J

@Temperature -196 °C
 >= 264 ft-lb

@Temperature -321 °F
 Notched
Thermal Properties Metric English Comments
CTE, linear 11.5 µm/m-°C

@Temperature 25.0 - 100 °C
 6.39 µin/in-°F

@Temperature 77.0 - 212 °F
11.9 µm/m-°C

@Temperature 25.0 - 200 °C
 6.61 µin/in-°F

@Temperature 77.0 - 392 °F
12.2 µm/m-°C

@Temperature 25.0 - 300 °C
 6.78 µin/in-°F

@Temperature 77.0 - 572 °F
12.5 µm/m-°C

@Temperature 25.0 - 400 °C
 6.94 µin/in-°F

@Temperature 77.0 - 752 °F
12.7 µm/m-°C

@Temperature 25.0 - 500 °C
 7.06 µin/in-°F

@Temperature 77.0 - 932 °F
12.7 µm/m-°C

@Temperature 25.0 - 600 °C
 7.06 µin/in-°F

@Temperature 77.0 - 1110 °F
Specific Heat Capacity 0.403 J/g-°C

@Temperature 25.0 °C
 0.0963 BTU/lb-°F

@Temperature 77.0 °F
0.416 J/g-°C

@Temperature 100 °C
 0.0994 BTU/lb-°F

@Temperature 212 °F
0.429 J/g-°C

@Temperature 200 °C
 0.103 BTU/lb-°F

@Temperature 392 °F
0.439 J/g-°C

@Temperature 300 °C
 0.105 BTU/lb-°F

@Temperature 572 °F
0.449 J/g-°C

@Temperature 400 °C
 0.107 BTU/lb-°F

@Temperature 752 °F
0.457 J/g-°C

@Temperature 600 °C
 0.109 BTU/lb-°F

@Temperature 1110 °F
0.461 J/g-°C

@Temperature 500 °C
 0.110 BTU/lb-°F

@Temperature 932 °F
Thermal Conductivity 9.30 W/m-K

@Temperature 25.0 °C
 64.5 BTU-in/hr-ft²-°F

@Temperature 77.0 °F
10.5 W/m-K

@Temperature 100 °C
 72.9 BTU-in/hr-ft²-°F

@Temperature 212 °F
11.9 W/m-K

@Temperature 200 °C
 82.6 BTU-in/hr-ft²-°F

@Temperature 392 °F
13.5 W/m-K

@Temperature 300 °C
 93.7 BTU-in/hr-ft²-°F

@Temperature 572 °F
14.9 W/m-K

@Temperature 400 °C
 103 BTU-in/hr-ft²-°F

@Temperature 752 °F
16.4 W/m-K

@Temperature 500 °C
 114 BTU-in/hr-ft²-°F

@Temperature 932 °F
17.5 W/m-K

@Temperature 600 °C
 121 BTU-in/hr-ft²-°F

@Temperature 1110 °F
Maximum Service Temperature, Air 427 °C
800 °F
Component Elements Properties Metric English Comments
Aluminum, Al <= 0.50 %
<= 0.50 %
Carbon, C <= 0.010 %
<= 0.010 %
Chromium, Cr 15 %
15 %
Iron, Fe <= 1.25 %
<= 1.25 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000126 ohm-cm

@Temperature 25.0 °C
 0.000126 ohm-cm

@Temperature 77.0 °F
0.000127 ohm-cm

@Temperature 100 °C
 0.000127 ohm-cm

@Temperature 212 °F
0.000127 ohm-cm

@Temperature 200 °C
 0.000127 ohm-cm

@Temperature 392 °F
0.000128 ohm-cm

@Temperature 300 °C
 0.000128 ohm-cm

@Temperature 572 °F
0.000128 ohm-cm

@Temperature 400 °C
 0.000128 ohm-cm

@Temperature 752 °F
0.000129 ohm-cm

@Temperature 500 °C
 0.000129 ohm-cm

@Temperature 932 °F
0.000131 ohm-cm

@Temperature 600 °C
 0.000131 ohm-cm

@Temperature 1110 °F