- SABIC Innovative Plastics LNP THERMOCOMP 9X11427
SABIC Innovative Plastics LNP THERMOCOMP 9X11427
| Category | Polymer , Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 9X11427.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* 9X11427 is a compound based on Miscellanbeous resin containing 40% specialty glass filled TP alloy. Added features of this grade include: Ultra-Stiff Toughness, Improved Impact, Good Flow for Thin Wall molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ASTM D792 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 141 MPa | 20500 psi | 5 mm/min; ISO 527 |
| 150 MPa | 21800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 14.3 GPa | 2070 ksi | 1 mm/min; ISO 527 |
| 14.6 GPa | 2120 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 219 MPa | 31800 psi | ISO 178 |
| 227 MPa | 32900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 229 MPa | 33200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 12.32 GPa | 1787 ksi | 2 mm/min; ISO 178 |
| 12.9 GPa | 1870 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.59 J/cm | 2.98 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.0 J/cm | 20.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
37.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Oxford Polymers OPX782 Polybutylene Terephthalate (PBT), Impact Modified/ Glass Beads
- Pau Tai UNISTAB RP-33K Solid Complex Stabilizer
- Fainplast Compounds RH 225 Rigid PVC, Antishock Extrusion
- Lubriplate NO.0 Petroleum-Based Machine Tool Oil
- Wellman Wellamid® MRGF25/15 42H-BK848 (Interior) 40% Mineral/Glass Fiber Reinforced, 848 Black Color Match Nylon 6
- Total PPC 5660 Propylene, Heterophasic Copolymer
- Diamond Polymers ABS 4500R
- Adell BJ-14 Nylon 6, 20% Glass Reinforced; High Impact
- DSM Akulon® F223-DH Nylon 6 (European Grade) (Cond) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved