- Chosun Refractories HSC-16S-W2 Dense and High-Strength Castable, Credens
Chosun Refractories HSC-16S-W2 Dense and High-Strength Castable, Credens
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HSC-16S-W2 Dense and High-Strength Castable, Credens.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.017658 GPa @Temperature 1000 °C, Time 10800 sec |
2.5611 ksi @Temperature 1830 °F, Time 3.00 hour |
|
| 0.01962 GPa @Temperature 110 °C, Time 86400 sec |
2.846 ksi @Temperature 230 °F, Time 24.0 hour |
||
| Compressive Strength | 10.8 MPa @Temperature 1000 °C, Time 10800 sec |
1560 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| 90.2 MPa @Temperature 110 °C, Time 86400 sec |
13100 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1600 °C | 2910 °F | limited |
| Shrinkage | -0.0300 % @Temperature 1350 °C, Time 10800 sec |
-0.0300 % @Temperature 2460 °F, Time 3.00 hour |
|
| -0.0200 % @Temperature 110 °C, Time 86400 sec |
-0.0200 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 65 % | 65 % | |
| CaO | 1.2 % | 1.2 % | |
| SiO2 | 30 % | 30 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 600 min | 2.00 - 10.0 hour | Setting Time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Vibrating, Casting | |
| Material Required for Estimating(kg/?) | 2,640 | |
| Water Required for Casting(%) | 5.2-5.6 |
Users viewing this material also viewed the following:
- MV Labs HF450 HfOCl2 ·8H2O Hafnium oxychloride hydrate
- Polimeri Europa Eraclene® ML 74 High Density Polyethylene - Injection Molding
- PolyOne Nymax™ GF 1200 A 43 Natural Polyamide 66 (Nylon 66)
- SABIC Innovative Plastics Lexan® FXD9810U PC Copolymer (Asia Pacific)
- DSM Akulon® S223-TP4 (Cond.) Impact Modified Nylon 66 (North America) (discontinued **)
- Humiseal 1C49 Silicone Conformal Coating
- Hexcel® HexForce™ GA060 Carbon Fabric
- ChevronTexaco Starplex® Moly NLGI Grade 1
- LNP Lubricomp® PDX-J-91198 Polyethersulfone, Proprietary Filler (discontinued **)
Copyright © lookpolymers.com All Rights Reserved