SABIC Innovative Plastics LNP Stat-loy 9X05426C PMMA (Asia Pacific)

Category Polymer , Thermoplastic , Acrylic (PMMA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Stat-loy
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Stat-loy 9X05426C PMMA (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
LNP* Stat-loy* 9X05426C is a compound based on PMMA resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
1.14 g/cc
0.0412 lb/in³
ASTM D 792
Linear Mold Shrinkage, Flow 0.0080 cm/cm

@Time 86400 sec
 0.0080 in/in

@Time 24.0 hour
 ASTM D 955
0.0082 cm/cm

@Time 86400 sec
 0.0082 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0098 cm/cm

@Time 86400 sec
 0.0098 in/in

@Time 24.0 hour
 ISO 294
0.010 cm/cm

@Time 86400 sec
 0.010 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 MPa
5660 psi
ISO 527
40.0 MPa
5800 psi
ASTM D 638
Tensile Strength, Yield 42.0 MPa
6090 psi
ASTM D 638
42.0 MPa
6090 psi
ISO 527
Elongation at Break 18.4 %
18.4 %
ASTM D 638
20.3 %
20.3 %
ISO 527
Elongation at Yield 6.2 %
6.2 %
ISO 527
6.7 %
6.7 %
ASTM D 638
Tensile Modulus 1.47 GPa
213 ksi
1 mm/min; ISO 527
1.75 GPa
254 ksi
50 mm/min; ASTM D 638
Flexural Strength 44.0 MPa
6380 psi
ISO 178
55.0 MPa
7980 psi
ASTM D 790
Flexural Modulus 1.41 GPa
205 ksi
ISO 178
1.66 GPa
241 ksi
ASTM D 790
Izod Impact, Notched 0.320 J/cm

@Temperature 23.0 °C
 0.599 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 5.39 J/cm

@Temperature 23.0 °C
 10.1 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 2.00 J

@Temperature 23.0 °C
 1.48 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 101 µm/m-°C

@Temperature -40.0 - 40.0 °C
 56.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
101 µm/m-°C

@Temperature -40.0 - 40.0 °C
 56.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 108 µm/m-°C

@Temperature -40.0 - 40.0 °C
 60.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
109 µm/m-°C

@Temperature -40.0 - 40.0 °C
 60.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 79.0 °C
174 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
79.0 °C

@Thickness 3.20 mm
 174 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
67.0 °C

@Thickness 3.20 mm
 153 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+9 - 1.00e+11 ohm-cm
1.00e+9 - 1.00e+11 ohm-cm
ASTM D 257
Surface Resistance 1.00e+9 - 1.00e+11 ohm
1.00e+9 - 1.00e+11 ohm
ASTM D 257