Bhansali Engineering Abstron AN-450 EVM Flame Retardant ABS Grade

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Bhansali Engineering Abstron AN-450 EVM Flame Retardant ABS Grade.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Bhansali
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D-955
Melt Flow 63 g/10 min
<br>@Load 10.0 kg,<br> Temperature 220 °C
 63 g/10 min
<br>@Load 22.0 lb,<br> Temperature 428 °F
 ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 106
106
ASTM D-785
Tensile Strength, Yield 41.2 MPa
<br>@Thickness 3.20 mm
 5970 psi
<br>@Thickness 0.126 in
 Type 1, 5 mm/min; ASTM D-638
Flexural Yield Strength 56.9 MPa
<br>@Thickness 6.40 mm
 8250 psi
<br>@Thickness 0.252 in
 ASTM D-790
Flexural Modulus 2.06 GPa
<br>@Thickness 6.40 mm
 299 ksi
<br>@Thickness 0.252 in
 ASTM D-790
Izod Impact, Notched 1.37 J/cm
<br>@Thickness 6.40 mm
 2.57 ft-lb/in
<br>@Thickness 0.252 in
 ASTM D-256
1.76 J/cm
<br>@Thickness 3.20 mm
 3.31 ft-lb/in
<br>@Thickness 0.126 in
 ASTM D-256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Method A - Annealed; ASTM D-648
Vicat Softening Point 99.0 °C
210 °F
Method B; ASTM D-1525
Flammability, UL94 V-0
<br>@Thickness 3.20 mm
 V-0
<br>@Thickness 0.126 in
 UL-94