LATI Latishield 66-08A G/25-V0KB1 PA66, Steel/Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | LATI |
| Trade Name | Latishield |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latishield 66-08A G/25-V0KB1 PA66, Steel/Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EMI shielding product based on Polyamide 66 (PA66). Steel fibers. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0035 - 0.0050 cm/cm | 0.0035 - 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0095 - 0.012 cm/cm | 0.0095 - 0.012 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | |
| Elongation at Break | 2.5 % | 2.5 % | |
| Tensile Modulus | 8.30 GPa | 1200 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| Charpy Impact, Notched | 0.750 J/cm² | 3.57 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | |
| Vicat Softening Point | 245 °C @Load 5.00 kg |
473 °F @Load 11.0 lb |
|
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
||
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||
| Oxygen Index | 28 % | 28 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 50 ohm | 50 ohm | |
| Comparative Tracking Index | 200 V | 200 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C | 194 - 212 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Electromagnetic reflection | 92 dB | |
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 4518 CU W 45% Mineral Filled Polypropylene
- Polykemi AB POLYfill PPH GF35040 D PP, Glass Fiber-Reinforced, Chemically Coupled, Detergent Resistant
- Akro-Plastic Akromid® S31 (3484) PA 6.10 Dry (discontinued **)
- Solvay Specialty Polymers Tecnoflon® PL 958 Fluoroelastomer
- Solvay DURAPHOS® 100 Octadecyl phosphonate
- Chengdu Polyster H3303 Thermoplastic Polyether-ester Elastomer (TPEE)
- DuPont Performance Polymers Rynite® RE15022 NC010 Polyethylene Terephthalate (PET)
- ExxonMobil Mobilgrease XTC
- ATI Allegheny Ludlum AL 29-4-2® Duplex Stainless Steel, UNS S44800
- Aclo Accutech Polyethylene HD0234G10UVL High Density Glass Reinforced UV Stabilized
Copyright © lookpolymers.com All Rights Reserved