SABIC Innovative Plastics LNP STAT-LOY AX06484 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY AX06484 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-LOY* AX06484 is a compound based on ABS resin containing Talc. Added feature of this grade is: Antistatic, Extrudeable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Moisture Absorption | 3.80 % | 3.80 % | 50% RH, 24 hrs; ASTM D570 |
| 5.60 % | 5.60 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa | 3630 psi | Type I, 5 mm/min; ASTM D638 |
| 26.0 MPa | 3770 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 5 mm/min; ISO 527 |
| 28.0 MPa | 4060 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.54 GPa | 368 ksi | 1 mm/min; ISO 527 |
| 3.12 GPa | 453 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 45.0 MPa | 6530 psi | ISO 178 |
| 50.0 MPa | 7250 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 51.0 MPa | 7400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.59 GPa | 376 ksi | 2 mm/min; ISO 178 |
| 2.75 GPa | 399 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.440 J/cm | 0.824 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.41 J/cm | 8.26 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
52.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 7.0 - 9.0 ohm | 7.0 - 9.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Hong Kun Group N-Propyl Bromide Additive
- Lehmann & Voss LUVOCOM® 1301-8456 PPS, linear, with glass fiber, PTFE, lubricant modified
- Lord Adhesives Fusor® 2001 / 2002 Urethane Adhesive
- Solvay Specialty Polymers Tecnoflon® FOR 421/U Fluoroelastomer
- Solvay RHODOPOL® T Surfactant
- Tra-Con Tra-Bond 526D01
- Bohler-Uddeholm BÖHLER S692/S693 MICROCLEAN® PM M4 High Speed Steel
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 420, Hardened + 649°C (1200°F) Temper
Copyright © lookpolymers.com All Rights Reserved