SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-LOY* 9X03508 is a compound based on PPO+PA66 resin containing Proprietary Filler(s). Added features of this material include: Antistatic, Flame Retardant, High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.900 % | 0.900 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ASTM D638 |
| 58.0 MPa | 8410 psi | ISO 527 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | ASTM D638 |
| 59.0 MPa | 8560 psi | ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| 2.8 % | 2.8 % | ISO 527 | |
| Elongation at Yield | 2.1 % | 2.1 % | ASTM D638 |
| 2.4 % | 2.4 % | ISO 527 | |
| Tensile Modulus | 4.47 GPa | 648 ksi | 1 mm/min; ISO 527 |
| 4.82 GPa | 699 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
| 96.0 MPa | 13900 psi | ISO 178 | |
| Flexural Modulus | 3.44 GPa | 499 ksi | ASTM D790 |
| 4.00 GPa | 580 ksi | ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 65.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 230 °C @Thickness 3.20 mm |
446 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 186 °C @Thickness 3.20 mm |
367 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+10 - 1.00e+12 ohm | 1.00e+10 - 1.00e+12 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 8101 Glass Reinforced Polyester BMC
- Plaskolite Optix® PL-200 Acrylic Resin (discontinued **)
- ICO Polymers ICOFLOâ„¢ 510-5058 1200 Micron LDPE Powder
- Styron PULSEâ„¢ 6000 BG PC/ABS Engineering Resin
- A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene
- Asahi Glass Fluon® LM-730AP LM-ETFE Fluororesin
- 3M Scotchkote™ 474 Epoxy Concrete Repair
- Teknor Apex Monprene® MP 1566 Thermoplastic Elastomer
- Bulk Molding Compounds BMC T40-4020-AQ High Strength Arc Quenching Molding Compound
Copyright © lookpolymers.com All Rights Reserved