- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Ineos ABS Lustran® 261 ABS, High-Impact Blending Grade
Ineos ABS Lustran® 261 ABS, High-Impact Blending Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 261 ABS, High-Impact Blending Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 261 resin is a natural, stiffer-flow, virgin blending grade of ABS (acrylonitrile butadiene styrene). It is designed for use with other high-impact ABS resins for drain, waste, and vent (DWV) pipe and fittings. Lustran® ABS 261 resin in natural color (000000) meets or exceeds ASTM D 3965 2-1-2-2-2 cell class requirements, and is listed under NSF Standard 14. Lustran® ABS 261 resin is also listed under CSA Standard B181.1.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM-D792 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Index; ASTM-D1238 |
| 11 g/10 min @Load 10.0 kg, Temperature 230 °C |
11 g/10 min @Load 22.0 lb, Temperature 446 °F |
Rate; ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ASTM-D638 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ASTM-D638 |
| Izod Impact, Notched | 1.12 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
2.10 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM-D256 |
| 2.56 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
4.80 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C @Thickness 6.40 mm |
214 °F @Thickness 0.252 in |
Annealed; ASTM-D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 243 °C | 450 - 469 °F | Injection Molding |
| 232 - 243 °C | 450 - 469 °F | Extrusion | |
| Mold Temperature | 43.0 - 66.0 °C | 109 - 151 °F | Injection Molding |
| Drying Temperature | 82.0 - 93.0 °C @Time 7200 sec |
180 - 199 °F @Time 2.00 hour |
|
| Moisture Content | <= 0.050 % | <= 0.050 % | |
| Dew Point | <= -29.0 °C | <= -20.2 °F | inlet air |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Pressure | Moderately High to High, Injection Molding | |
| Injection Speed | Moderate to Fast | Injection Molding |
| Screw Compression Ratio | 2.4-2.8:1 | Extrusion |
| Screw Length-to-Diameter Ratio | 24-36:1 | Extrusion |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 FRC 2 LI PA6, flame retardant
- Park Electrochemical Nelco® N8000Q Cyanate Ester Epoxy Laminate and Prepreg
- PolyOne Geon™ Vinyl Flexible XV3847 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Pasargad Polymer Peyvand Pasamid 3P-H2130B Nylon 66, 30% Glass Fiber Reinforced
- Solvay Specialty Polymers Ixef® 2057 Polyarylamide (PARA), 45% Mineral Filler (discontinued **)
- IBC Advanced Alloys 42C Beryllium Nickel Casting Alloy
- LG Chemical LUMID GP2430A(W) PA6+GF43%, General Purpose
- SABIC Innovative Plastics LNP Stat-kon DEP32XXC PC
- Eagle Brass 230 Red Brass, Spring
- Barlog Plastics KEBAFLEX SG 60 A.01 black TPE-S, Shore A60, black
Copyright © lookpolymers.com All Rights Reserved