SABIC Innovative Plastics LNP STAT-KON Ultem_UC1200 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON Ultem_UC1200 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-kon* Ultem_UC1200 compound is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0012 - 0.0022 cm/cm

@Thickness 3.20 mm
 0.0012 - 0.0022 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0050 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 7.5 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 7.5 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 131 MPa
19000 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 131 MPa
19000 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 5.1 %
5.1 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 5.1 %
5.1 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 8.13 GPa
1180 ksi
5 mm/min; ASTM D638
Flexural Strength 193 MPa
28000 psi
2.6 mm/min, 100 mm span; ASTM D790
221 MPa
32100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 7.83 GPa
1140 ksi
1.3 mm/min, 50 mm span; ASTM D790
8.27 GPa
1200 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.16 J/cm
7.79 ft-lb/in
ASTM D4812
Dart Drop, Total Energy 6.00 J

@Temperature 23.0 °C
 4.43 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 8.00 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
14.4 µm/m-°C

@Temperature -20.0 - 150 °C
 8.00 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
CTE, linear, Transverse to Flow 32.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 18.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
39.6 µm/m-°C

@Temperature -20.0 - 150 °C
 22.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 213 °C

@Thickness 3.20 mm
 415 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 208 °C

@Thickness 3.20 mm
 406 °F

@Thickness 0.126 in
 unannealed; ASTM D648
210 °C

@Thickness 6.40 mm
 410 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 214 °C
417 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 105 °C
221 °F
UL 746B
UL RTI, Mechanical with Impact 105 °C
221 °F
UL 746B
UL RTI, Mechanical without Impact 105 °C
221 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.57 mm
 V-0

@Thickness 0.0618 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 400 ohm-cm
400 ohm-cm
ASTM D257
Surface Resistance 200000 ohm
200000 ohm
ASTM D257
Static Decay 0.010 sec
0.010 sec
5000V to <50V; FTMS101B
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 30 - 60 arcs
30 - 60 arcs
UL 746A