SABIC Innovative Plastics Lexan® FL2003 PC (Asia Pacific)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Lexan®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Lexan® FL2003 PC (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Various weight reductions at 0.250" (6.35mm) wall. Low temperature impact and high heat resistant. Excellent surface. UV-stabilized.This data was supplied by SABIC-IP for the Asia Pacific region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.09 g/cc	1.09 g/cc	foam molded; ASTM D 792
	1.21 g/cc	1.21 g/cc	ASTM D 792
Water Absorption	0.13 % @Time 86400 sec	0.13 % @Time 24.0 hour	ASTM D 570
Moisture Absorption at Equilibrium	0.34 % @Temperature 23.0 °C	0.34 % @Temperature 73.4 °F	ASTM D 570
Linear Mold Shrinkage, Flow	0.0060 - 0.0080 cm/cm @Thickness 6.40 mm	0.0060 - 0.0080 in/in @Thickness 0.252 in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	53.0 MPa @Thickness 6.35 mm	7690 psi @Thickness 0.250 in	ASTM D 638
Elongation at Break	7.8 % @Thickness 6.35 mm	7.8 % @Thickness 0.250 in	ASTM D 638
Tensile Modulus	2.30 GPa @Thickness 6.40 mm	334 ksi @Thickness 0.252 in	ASTM D 638
Flexural Yield Strength	75.0 MPa @Thickness 6.40 mm	10900 psi @Thickness 0.252 in	ASTM D 790
Flexural Modulus	1.93 GPa @Thickness 6.40 mm	280 ksi @Thickness 0.252 in	ASTM D 790
Izod Impact, Unnotched	26.7 J/cm @Temperature 23.0 °C	50.0 ft-lb/in @Temperature 73.4 °F	ASTM D 4812
Dart Drop, Total Energy	122 J @Temperature 23.0 °C	90.0 ft-lb @Temperature 73.4 °F	SABIC Method

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	55.8 µm/m-°C @Temperature -40.0 - 95.0 °C	31.0 µin/in-°F @Temperature -40.0 - 203 °F	ASTM E 831
Specific Heat Capacity	1.18 J/g-°C	0.282 BTU/lb-°F	ASTM C 351
Deflection Temperature at 0.46 MPa (66 psi)	137 °C @Thickness 6.40 mm	279 °F @Thickness 0.252 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	126 °C @Thickness 6.40 mm	259 °F @Thickness 0.252 in	unannealed; ASTM D 648
UL RTI, Electrical	80.0 °C	176 °F	UL 746B
UL RTI, Mechanical with Impact	80.0 °C	176 °F	UL 746B
UL RTI, Mechanical without Impact	80.0 °C	176 °F	UL 746B
Flammability, UL94	HB @Thickness 5.99 mm	HB @Thickness 0.236 in	UL 94
Oxygen Index	28.2 %	28.2 %	LOI; ASTM D 2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.60e+16 ohm-cm	3.60e+16 ohm-cm	ASTM D 257
Surface Resistance	>= 1.10e+17 ohm	>= 1.10e+17 ohm	ASTM D 257
Dielectric Constant	2.47 @Frequency 100 Hz	2.47 @Frequency 100 Hz	ASTM D 150
	2.68 @Frequency 1.00e+6 Hz	2.68 @Frequency 1.00e+6 Hz	ASTM D 150
Dissipation Factor	0.0037 @Frequency 100 Hz	0.0037 @Frequency 100 Hz	ASTM D 150
	0.0039 @Frequency 1.00e+6 Hz	0.0039 @Frequency 1.00e+6 Hz	ASTM D 150

Descriptive Properties	Value	Comments
FOAM - ELECTRICAL 6.4 mm Wt Reduction, %	20	-
FOAM - Flame Class Minimum Density, g/cm^3	1.12	-
FOAM - IMPACT 6.4 mm Wt Reduction, %	10	-
FOAM - MECHANICAL 6.4 mm Wt Reduction, %	10	-
FOAM - PHYSICAL 6.4mm Wt Reduction, %	10	-
FOAM - THERMAL 6.4mm Wt Reduction, %	10	-
UV-light, water exposure/immersion	F1	UL 746C