LyondellBasell Moplen HP400L Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | LyondellBasell |
| Trade Name | Moplen |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Moplen HP400L Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: All ingredients in HP400L meet the chemical registration requirements of TSCA (U.S.) and DSL (Canada). Uses: Toys, containers, lids, medical applications, closure capsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D792 & ISO 1183 |
| Melt Flow | 5.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 89 | 89 | ASTM D 785 |
| Hardness, Shore D | 73 | 73 | ISO 868 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-1, 2 |
| 35.2 MPa | 5100 psi | ASTM D 638 | |
| Elongation at Yield | 10 % | 10 % | ASTM D 638 |
| Flexural Modulus | 1.59 GPa | 230 ksi | 1% Secant, 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | 73°F; ASTM D256 |
| 0.763 J/cm | 1.43 ft-lb/in | 73°F, Type 1, Notch A; ISO 180 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.1 °C | 124 °F | Unannealed; ISO 75A-1, -2 |
| Vicat Softening Point | 155 °C | 311 °F | Method A; ISO 306 |
| UL RTI, Electrical | 221 °C | 430 °F | 0.028 in; UL 746 |
| UL RTI, Mechanical with Impact | 221 °C | 430 °F | 0.028 in; UL 746 |
| UL RTI, Mechanical without Impact | 221 °C | 430 °F | 0.028 in; UL 746 |
| Flammability, UL94 | HB @Thickness 0.711 mm |
HB @Thickness 0.0280 in |
NC |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® DMX1214 PC Copolymer (Asia Pacific)
- DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 60 Gauge (discontinued **)
- Reliance Industries Repol H029SP Polypropylene
- Lehmann & Voss LUVOCOM® 80-7388 Polyacetal-copolymer, with carbon fiber and PTFE
- Kennametal Stellite Stellite® 98M2 cast
- Kostat ICP-STAT ICD-1005 ABS Sheet
- Techmer ES HiFill® PA6 GF/M15 A1 BK 15% Glass/Mineral Filled
- CeramTec Sonox® P508 Piezoceramic
- 3M 32665 Green Heavy Duty Performance Coating - Part B
- Dow PELLETHANE® 2104-65D Polyurethane Elastomer (Ether-Ether Hybrid) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved