- LyondellBasell Hifaxâ„¢ CJ232 Thermoplastic Olefin Resin
LyondellBasell Hifaxâ„¢ CJ232 Thermoplastic Olefin Resin
| Category | Polymer , Thermoplastic |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ CJ232 Thermoplastic Olefin Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features: medium high melt flow, medium modulus, low CLTE, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good dimensional stability, paintableApplications: body side moldings, appliquesDescription: Hifax CJ232 medium high melt flow, low CLTE, paintable thermoplastic elastomeric olefin resin has an exceptional combination of stiffness, impact resistance and dimensional stability. It was desigend primarliy for auotmotive exterior ornamentation applications requiring low thermal expansion characteristics and a moderate degress of flexiblity.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Tool, Montell |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 59 | 59 | ISO 868 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ISO R527-1 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO R527-1 |
| Elongation at Break | 500 % | 500 % | ISO R527-1 |
| Elongation at Yield | 10 % | 10 % | ISO R527-1 |
| Flexural Modulus | 0.750 GPa | 109 ksi | ISO 178 |
| Izod Impact, Notched | 0.600 J/cm @Temperature -40.0 °C |
1.12 ft-lb/in @Temperature -40.0 °F |
ISO 180 |
| Impact Test | 23.0 J @Temperature -30.0 °C |
17.0 ft-lb @Temperature -22.0 °F |
MAII, E at Max Load, Ductile; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 100 °C |
25.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.0 °C | 109 °F | ISO 75 |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FL 24 Low Density Polyethylene - Blown Film Extrusion
- Palm Labs Adhesives TURBO FUSE SERIES 190 CLEAR FLEXIBLE (4000 Viscosity) Rapid Bonding Adhesive
- Lehmann & Voss LUVOCOM® 50-7586 Polycarbonate, with carbon fiber
- Momentive Performance Materials Siloprenâ„¢ FSL 7661 Fluorinated Liquid Silicone Rubber
- SABIC Innovative Plastics NORYL WCA875 PPE-TPE (Asia Pacific)
- Solvay TECHNYL® B 50 H1 PA66/6, Conditioned
- SABIC Innovative Plastics LNP STAT-KON OE006C1 PPS - Linear
- A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene
- A. Schulman POLYBATCH™ Beige 60199 Concentrate Based In LLDPE
- Bhansali Engineering Abstron IM17A TT ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved