SABIC Innovative Plastics LNP STAT-KON RE006 PA6.6 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON RE006 PA6.6 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON RE006 is a compound based on Nylon 66 containing carbon fiber. Added features of this material include: Electrically Conductive. Also known as STAT-KON RC-1006
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 273 MPa | 39600 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 407 MPa | 59000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 21.0 GPa | 3050 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 11.74 J/cm | 21.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 ohm | 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Nanocyl EPOCYL™ NC R1MY-04 Master Batch Liquid tetrafunctional epoxy Resin for solvent based Formulation Purposes: Dilution Factor 6
- Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Aerospace Silica Fabric Reinforced
- Teknor Apex Telcar® TL-2560A Thermoplastic Elastomer
- Chase Plastics CP Pryme® NN300HSL (DAM) Nylon 66 (Utility Grade), Heat Stabilized, Internally Lubricated
- Loctite® 3534 Glob Top Encapsulant
- China Tungsten YG813 Tungsten Carbide
- DuPont Performance Polymers Zytel® 101F BKB009 Nylon 66 (Unverified Data**)
- Potters Industries Conduct-O-Fil® SA300S30 Silver-coated Aluminum Granules
- BASF Novolen® 3248 RC Polypropylene
- Lubrizol ESTANE® 58206 Ester Based Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved