SABIC Innovative Plastics LNP STAT-KON Noryl_FMC1010 PPE+PS

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP STAT-KON
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP STAT-KON Noryl_FMC1010 PPE+PS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Stat-kon* Noryl_FMC1010 compound is a 10% carbon fiber, static dissipative, foamable resin Nonchlorinated, nonbrominated. UL94 V1 rated. Property values at 20% WR, 0.250"" wall.

Physical Properties	Metric	English	Comments
Specific Gravity	0.920 g/cc	0.920 g/cc	foam molded; ASTM D792
	1.15 g/cc	1.15 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0015 - 0.0025 cm/cm @Thickness 3.20 mm	0.0015 - 0.0025 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0020 - 0.0040 cm/cm @Thickness 3.20 mm	0.0020 - 0.0040 in/in @Thickness 0.126 in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	45.0 MPa @Thickness 6.35 mm	6530 psi @Thickness 0.250 in	ASTM D638
Elongation at Break	4.1 % @Thickness 6.35 mm	4.1 % @Thickness 0.250 in	ASTM D638
Flexural Yield Strength	95.0 MPa	13800 psi	6.4 mm; ASTM D790
Flexural Modulus	5.99 GPa	869 ksi	6.4 mm; ASTM D790
Izod Impact, Unnotched	1.54 J/cm @Thickness 6.40 mm	2.89 ft-lb/in @Thickness 0.252 in	ASTM D4812

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	103 °C @Thickness 6.40 mm	217 °F @Thickness 0.252 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	97.0 °C @Thickness 6.40 mm	207 °F @Thickness 0.252 in	unannealed; ASTM D648
UL RTI, Electrical	50.0 °C	122 °F	UL 746B
UL RTI, Mechanical with Impact	50.0 °C	122 °F	UL 746B
UL RTI, Mechanical without Impact	50.0 °C	122 °F	UL 746B
Flammability, UL94	V-1 @Thickness 3.98 mm	V-1 @Thickness 0.157 in	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	8000 ohm-cm	8000 ohm-cm	ASTM D257
Surface Resistance	13000 ohm	13000 ohm	ASTM D257

Descriptive Properties	Value	Comments
FOAM - ELECTRICAL 6.4 mm Wt Reduction	20%
FOAM - Flame Class Minimum Density	0.96g/cm^3
FOAM - IMPACT 6.4 mm Wt Reduction	20%
FOAM - MECHANICAL 6.4 mm Wt Reduction	20%
FOAM - PHYSICAL 6.4mm Wt Reduction	20%
FOAM - THERMAL 6.4mm Wt Reduction	20%