SABIC Innovative Plastics LNP VERTON RV007ESS PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RV007ESS PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP VERTON* RF-7007 EM HS is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.970 % | 0.970 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 204 MPa | 29600 psi | ASTM D638 |
| 214 MPa | 31000 psi | ISO 527 | |
| Elongation at Break | 2.1 % | 2.1 % | ISO 527 |
| Tensile Modulus | 11.97 GPa | 1736 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 309 MPa | 44800 psi | ISO 178 |
| Flexural Modulus | 9.88 GPa | 1430 ksi | ASTM D790 |
| 10.24 GPa | 1485 ksi | ISO 178 | |
| Izod Impact, Notched | 2.77 J/cm | 5.19 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| 25.0 kJ/m² @Temperature -40.0 °C |
11.9 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 245 °C @Thickness 3.20 mm |
473 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2243-24 CR-SX Fiberglass Reinforced Thermoset Thick Molding Compound
- Overview of materials for Phenolic, Novolac, Impact Grade, Filled
- Garlock GYLON® 3522 PTFE Diaphragm
- Gouda Vuurvast VIBRON 130 Dense Vibrating Refractory Castable
- Techmer ES HiFill® PA6/12 CF30 BK 30% Carbon Filled
- UBE UBEPOL BR130B Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 35 Minutes at 145°C)
- ACC EP Primer 28 EPI Engineered Polymers Aromatic polyisocyanate Prepolymer
- Vyncolit Neopreg Kinel® SK4504 S12 Carbon Reinforced Molding Compound
- Karina E 842-18/106-Y-RT-POWDER Compound PVC Gray
Copyright © lookpolymers.com All Rights Reserved