SABIC Innovative Plastics LNP STAT-KON MD000ISC PP

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON MD000ISC PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* MD000ISC is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact.
Physical Properties Metric English Comments
Density 0.970 g/cc
0.0350 lb/in³
ISO 1183
0.980 g/cc
0.0354 lb/in³
ASTM D792
Moisture Absorption 0.0300 %
0.0300 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.016 - 0.018 cm/cm

@Time 86400 sec
 0.016 - 0.018 in/in

@Time 24.0 hour
 ASTM D955
0.016 - 0.018 cm/cm

@Time 86400 sec
 0.016 - 0.018 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0158 - 0.018 cm/cm

@Time 86400 sec
 0.0158 - 0.018 in/in

@Time 24.0 hour
 ISO 294
0.016 - 0.018 cm/cm

@Time 86400 sec
 0.016 - 0.018 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 17.0 MPa
2470 psi
ASTM D638
17.0 MPa
2470 psi
ISO 527
Tensile Strength, Yield 18.0 MPa
2610 psi
ISO 527
21.0 MPa
3050 psi
ASTM D638
Elongation at Break 133.8 %
133.8 %
ASTM D638
Elongation at Yield 9.0 %
9.0 %
ASTM D638
Tensile Modulus 0.480 GPa
69.6 ksi
50 mm/min; ASTM D638
1.10 GPa
160 ksi
1 mm/min; ISO 527
Flexural Strength 27.0 MPa
3920 psi
ASTM D790
27.0 MPa
3920 psi
ISO 178
Flexural Modulus 1.13 GPa
164 ksi
ASTM D790
1.20 GPa
174 ksi
ISO 178
Izod Impact, Notched 8.33 J/cm
15.6 ft-lb/in
ASTM D256
Izod Impact, Unnotched 15.53 J/cm
29.09 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 65.0 kJ/m²
30.9 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 112 kJ/m²
53.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 24.0 J
17.7 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 31.0 J
22.9 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 101 µm/m-°C

@Temperature -40.0 - 40.0 °C
 56.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
101 µm/m-°C

@Temperature -40.0 - 40.0 °C
 56.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 119 µm/m-°C

@Temperature -40.0 - 40.0 °C
 66.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
119 µm/m-°C

@Temperature -40.0 - 40.0 °C
 66.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 81.0 °C

@Thickness 3.20 mm
 178 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 56.0 °C
133 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
52.0 °C

@Thickness 3.20 mm
 126 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 10 - 1.00e+6 ohm
10 - 1.00e+6 ohm
ASTM D257
Static Decay 0.010 sec
0.010 sec
5000V to <50V; FTMS101B