- Acetal Copolymer, 30% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP KFL25 Acetal Copolymer
SABIC Innovative Plastics LNP LUBRICOMP KFL25 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KFL25 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* KFL25 is a compound based on Acetal Copolymer resin containing 25% Glass Fiber, 10% PTFE. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ASTM D792 |
| 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.190 % | 0.190 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0096 cm/cm @Time 86400 sec |
0.0096 in/in @Time 24.0 hour |
ISO 294 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ISO 527 |
| 85.0 MPa | 12300 psi | ASTM D638 | |
| Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
| 1.3 % | 1.3 % | ISO 527 | |
| Tensile Modulus | 9.87 GPa | 1430 ksi | 1 mm/min; ISO 527 |
| 10.24 GPa | 1485 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| 131 MPa | 19000 psi | ASTM D790 | |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ASTM D790 |
| 9.20 GPa | 1330 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.93 J/cm | 5.49 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 82.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 82.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 63.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 63.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JD455CJ Polyvinyl Chloride, Flexible (PVC, Flexible)
- MV Labs NI1000 NiSO4·7H2O Nickel sulfate heptahydrate
- Polymer Resources NY6-G33-[color]-H Nylon 6, 33% Glass Reinforced, Heat Stabilized
- Materion Beryllium Copper Alloy M25 Wire; 1/2HT (TH02) Temper; 1.3-12.7 mm Diameter (UNS C17300)
- Techmer ES HiFill® PA6 GF33 L NAT004 33% Glass Filled
- SABIC Innovative Plastics Noryl GTX GTX977 PPE+PA66 (Europe-Africa-Middle East)
- Arlon 51576R015A 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Chem Polymer Chemlon 115 G Nylon 66, 15% Glass Fiber Reinforced
- ArcelorMittal Extragal® Z200 Double-sided pure zinc galvanized steel
Copyright © lookpolymers.com All Rights Reserved