SABIC Innovative Plastics LNP Lubricomp KFL34 Acetal Copolymer (Asia Pacific)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled , Acetal Homopolymer, Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp KFL34 Acetal Copolymer (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* KFL34 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0048 cm/cm @Time 86400 sec |
0.0048 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0107 cm/cm @Time 86400 sec |
0.0107 in/in @Time 24.0 hour |
ISO 294 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ASTM D 638 |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D 638 |
| Tensile Modulus | 7.23 GPa | 1050 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D 790 |
| Flexural Modulus | 6.05 GPa | 877 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.420 J/cm @Temperature 23.0 °C |
0.787 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.25 J/cm @Temperature 23.0 °C |
7.96 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.50 | 0.50 | ASTM D 3702 Modified |
| K (wear) Factor | 399 x 10-8 mm³/N-M | 198 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 159 °C @Thickness 3.20 mm |
318 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 5 FRA 5 Polyamide 6, 5% Glass Fiber, Halogen Flame Retardant
- Orion Engineered Carbons CK3 Carbon Black
- Qualchem Danamid AFGF-30 Polyamide 66, 30% Glass Fiber
- MarkeTech Cu/Mo/Cu 1:3:1 Laminated Sheet
- Idemitsu Kosan Xarec® N WA 7030 SPS, 30% Glass Filled
- SK Chemicals SKYTHANE® T850A Polyester Based, Low Hardness Thermoplastic Polyurethane Elastomer
- Solvay GERONOL® FF/4 Surfactant
- SABIC Innovative Plastics LNP STAT-KON DX92002 PC (Europe-Africa-Middle East)
- ChevronTexaco Bright-Cut® NM Metal Working Fluid
- 3M FM157 Indoor UL Recognized Computer Imprintable Silver Polyester Label Product
Copyright © lookpolymers.com All Rights Reserved