SABIC Innovative Plastics LNP STAT-KON KD000 Acetal Copolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON KD000 Acetal Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* KD000 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ASTM D792
1.45 g/cc
0.0524 lb/in³
ISO 1183
Moisture Absorption 0.280 %
0.280 %
50% RH, 24 hrs; ASTM D570
0.330 %
0.330 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.012 - 0.013 cm/cm
0.012 - 0.013 in/in
mold temp=60°C; SABIC Method
0.015 - 0.016 cm/cm
0.015 - 0.016 in/in
mold temp=100°C; SABIC Method
0.015 - 0.035 cm/cm

@Time 86400 sec
0.015 - 0.035 in/in

@Time 24.0 hour
ASTM D955
0.015 - 0.035 cm/cm

@Time 86400 sec
0.015 - 0.035 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0090 - 0.010 cm/cm
0.0090 - 0.010 in/in
mold temp=60°C; SABIC Method
0.011 - 0.012 cm/cm
0.011 - 0.012 in/in
mold temp=100°C; SABIC Method
0.015 - 0.035 cm/cm

@Time 86400 sec
0.015 - 0.035 in/in

@Time 24.0 hour
ASTM D955
0.015 - 0.035 cm/cm

@Time 86400 sec
0.015 - 0.035 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa
6820 psi
ISO 527
54.0 MPa
7830 psi
ASTM D638
Tensile Strength, Yield 53.0 MPa
7690 psi
ISO 527
58.0 MPa
8410 psi
ASTM D638
Elongation at Break 7.2 %
7.2 %
ASTM D638
20 %
20 %
ISO 527
Elongation at Yield 3.6 %
3.6 %
ASTM D638
5.0 %
5.0 %
ISO 527
Tensile Modulus 3.00 GPa
435 ksi
1 mm/min; ISO 527
3.50 GPa
508 ksi
50 mm/min; ASTM D638
Flexural Strength 82.0 MPa
11900 psi
ISO 178
95.0 MPa
13800 psi
ASTM D790
Flexural Modulus 3.20 GPa
464 ksi
ISO 178
3.25 GPa
471 ksi
ASTM D790
Izod Impact, Notched 0.350 J/cm
0.656 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.00 J/cm
15.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 37.0 kJ/m²
17.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 101 µm/m-°C

@Temperature -40.0 - 40.0 °C
56.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
102 µm/m-°C

@Temperature -40.0 - 40.0 °C
56.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 101 µm/m-°C

@Temperature -40.0 - 40.0 °C
56.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
101 µm/m-°C

@Temperature -40.0 - 40.0 °C
56.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
108 °C

@Thickness 3.20 mm
226 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 0.700 mm
HB

@Thickness 0.0276 in
UL 94
Electrical Properties Metric English Comments
Surface Resistance 100 - 10000 ohm
100 - 10000 ohm
ASTM D257