Shinkong Synthetic Fibers Shinite® T101G45 PET, 45% Glass Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 50% Glass Reinforced |
| Manufacturer | Shinkong Synthetic Fibers Corp |
| Trade Name | Shinite® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shinkong Synthetic Fibers Shinite® T101G45 PET, 45% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information from Shinkong Synthetic Fibers Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.67 g/cc | 1.67 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 137 MPa | 19900 psi | ASTM D638 |
| Elongation at Break | 3.6 % | 3.6 % | ASTM D638 |
| Flexural Yield Strength | 226 MPa | 32700 psi | ASTM D790 |
| Flexural Modulus | 12.6 GPa | 1820 ksi | ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.84 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 | 4.0 | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3946 TPE, PP Overmold or Standalone use
- Cookson Group Plaskon® 435 Mineral Filled Epoxy Molding Compound (discontinued **)
- Quantum Composites QC-2130 Phenolic 25% Glass Fiber SMC (discontinued **)
- Gouda Vuurvast CURON 140 GM Dense Refractory Castable
- IRPC Polimaxx Polene 120PC Styrene Acrylonitrile
- Solvay CATAFOR® CA80 Surfactant
- Dow Corning 1598 Performance Modifier
- 3M 8427-16 Cold Shrink Connector Insulators
- Wanhua Chemical Wanthane® WHT-1580 Polyester Based TPU
Copyright © lookpolymers.com All Rights Reserved