BASF Ultrason S 2010 G6 30% Glass Filled PSU

Category Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, 30% Glass Fiber Reinforced
Manufacturer BASF
Trade Name Ultrason S
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultrason S 2010 G6 30% Glass Filled PSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultrason S 2010 G6 is a 30% glass reinforced, medium viscosity injection molding PSU grade with high rigidity and strength.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ISO 1183
Water Absorption 0.60 %
0.60 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Viscosity Test 63 cm³/g
63 cm³/g
Viscosity number
Linear Mold Shrinkage, Flow 0.0029 cm/cm
0.0029 in/in
ISO 294
Linear Mold Shrinkage, Transverse 0.0046 cm/cm
0.0046 in/in
ISO 294
Melt Flow 30 g/10 min

@Load 10.0 kg,
Temperature 360 °C
 30 g/10 min

@Load 22.0 lb,
Temperature 680 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 193 MPa
28000 psi
ISO 2039-1
Tensile Strength at Break 120 MPa
17400 psi
5mm/min; ISO 527-2
52.0 MPa

@Temperature 160 °C
 7540 psi

@Temperature 320 °F
80.0 MPa

@Temperature 120 °C
 11600 psi

@Temperature 248 °F
120 MPa

@Temperature 40.0 °C
 17400 psi

@Temperature 104 °F
125 MPa

@Temperature 0.000 °C
 18100 psi

@Temperature 32.0 °F
Tensile Stress 50.0 MPa

@Strain 0.600 %,
Temperature 23.0 °C
 7250 psi

@Strain 0.600 %,
Temperature 73.4 °F
50.0 MPa

@Strain 1.70 %,
Temperature 160 °C
 7250 psi

@Strain 1.70 %,
Temperature 320 °F
55.0 MPa

@Strain 1.00 %,
Temperature 160 °C
 7980 psi

@Strain 1.00 %,
Temperature 320 °F
80.0 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 11600 psi

@Strain 1.00 %,
Temperature 73.4 °F
105 MPa

@Strain 1.50 %,
Temperature 23.0 °C
 15200 psi

@Strain 1.50 %,
Temperature 73.4 °F
Tensile Strength, Yield 120 MPa
17400 psi
50mm/min; ISO 527-2
Elongation at Break 1.7 %
1.7 %
5mm/min; ISO 527-2
Elongation at Yield 1.7 %
1.7 %
50mm/min; ISO 527-2
0.20 %

@Time 3600 sec,
Pressure 10.0 MPa
 0.20 %

@Time 1.00 hour,
Pressure 1450 psi
 140°C; ISO 899
0.20 %

@Time 3600 sec,
Pressure 15.0 MPa
 0.20 %

@Time 1.00 hour,
Pressure 2180 psi
 ISO 899
0.20 %

@Pressure 15.0 MPa,
Time 360000 sec
 0.20 %

@Pressure 2180 psi,
Time 100 hour
 ISO 899
0.20 %

@Pressure 15.0 MPa,
Time 3.60e+7 sec
 0.20 %

@Pressure 2180 psi,
Time 10000 hour
 ISO 899
0.25 %

@Pressure 10.0 MPa,
Time 360000 sec
 0.25 %

@Pressure 1450 psi,
Time 100 hour
 140°C; ISO 899
0.30 %

@Pressure 10.0 MPa,
Time 3.60e+7 sec
 0.30 %

@Pressure 1450 psi,
Time 10000 hour
 140°C; ISO 899
0.30 %

@Time 3600 sec,
Pressure 20.0 MPa
 0.30 %

@Time 1.00 hour,
Pressure 2900 psi
 140°C; ISO 899
0.35 %

@Pressure 20.0 MPa,
Time 360000 sec
 0.35 %

@Pressure 2900 psi,
Time 100 hour
 140°C; ISO 899
0.39 %

@Time 3600 sec,
Pressure 30.0 MPa
 0.39 %

@Time 1.00 hour,
Pressure 4350 psi
 ISO 899
0.40 %

@Time 3600 sec,
Pressure 30.0 MPa
 0.40 %

@Time 1.00 hour,
Pressure 4350 psi
 140°C; ISO 899
0.40 %

@Pressure 30.0 MPa,
Time 360000 sec
 0.40 %

@Pressure 4350 psi,
Time 100 hour
 ISO 899
0.41 %

@Pressure 30.0 MPa,
Time 3.60e+7 sec
 0.41 %

@Pressure 4350 psi,
Time 10000 hour
 ISO 899
0.50 %

@Pressure 20.0 MPa,
Time 3.60e+7 sec
 0.50 %

@Pressure 2900 psi,
Time 10000 hour
 140°C; ISO 899
0.50 %

@Pressure 30.0 MPa,
Time 360000 sec
 0.50 %

@Pressure 4350 psi,
Time 100 hour
 140°C; ISO 899
0.50 %

@Time 3600 sec,
Pressure 40.0 MPa
 0.50 %

@Time 1.00 hour,
Pressure 5800 psi
 140°C; ISO 899
0.55 %

@Pressure 40.0 MPa,
Time 360000 sec
 0.55 %

@Pressure 5800 psi,
Time 100 hour
 140°C; ISO 899
0.59 %

@Time 3600 sec,
Pressure 45.0 MPa
 0.59 %

@Time 1.00 hour,
Pressure 6530 psi
 ISO 899
0.60 %

@Pressure 45.0 MPa,
Time 360000 sec
 0.60 %

@Pressure 6530 psi,
Time 100 hour
 ISO 899
0.60 %

@Time 3600 sec,
Pressure 45.0 MPa
 0.60 %

@Time 1.00 hour,
Pressure 6530 psi
 140°C; ISO 899
0.61 %

@Pressure 45.0 MPa,
Time 3.60e+7 sec
 0.61 %

@Pressure 6530 psi,
Time 10000 hour
 ISO 899
0.80 %

@Time 3600 sec,
Pressure 60.0 MPa
 0.80 %

@Time 1.00 hour,
Pressure 8700 psi
 ISO 899
0.82 %

@Pressure 60.0 MPa,
Time 360000 sec
 0.82 %

@Pressure 8700 psi,
Time 100 hour
 ISO 899
0.90 %

@Pressure 60.0 MPa,
Time 3.60e+7 sec
 0.90 %

@Pressure 8700 psi,
Time 10000 hour
 ISO 899
0.90 %

@Pressure 30.0 MPa,
Time 3.60e+7 sec
 0.90 %

@Pressure 4350 psi,
Time 10000 hour
 140°C; ISO 899
1.2 %

@Time 3600 sec,
Pressure 80.0 MPa
 1.2 %

@Time 1.00 hour,
Pressure 11600 psi
 ISO 899
1.35 %

@Pressure 80.0 MPa,
Time 360000 sec
 1.35 %

@Pressure 11600 psi,
Time 100 hour
 ISO 899
1.4 %

@Pressure 40.0 MPa,
Time 3.60e+7 sec
 1.4 %

@Pressure 5800 psi,
Time 10000 hour
 140°C; ISO 899
1.55 %

@Pressure 80.0 MPa,
Time 3.60e+7 sec
 1.55 %

@Pressure 11600 psi,
Time 10000 hour
 ISO 899
1.6 %

@Pressure 45.0 MPa,
Time 3.60e+7 sec
 1.6 %

@Pressure 6530 psi,
Time 10000 hour
 140°C; ISO 899
1.9 %

@Pressure 45.0 MPa,
Time 360000 sec
 1.9 %

@Pressure 6530 psi,
Time 100 hour
 140°C; ISO 899
Creep Strength 23.0 MPa

@Time 3.60e+7 sec
 3340 psi

@Time 10000 hour
 in water at 95°C
30.0 MPa

@Time 3.60e+6 sec
 4350 psi

@Time 1000 hour
 in water at 95°C
40.0 MPa

@Time 360000 sec
 5800 psi

@Time 100 hour
 in water at 95°C
51.0 MPa

@Time 36000 sec
 7400 psi

@Time 10.0 hour
 in water at 95°C
Modulus of Elasticity 7.50 GPa

@Temperature 160 °C
 1090 ksi

@Temperature 320 °F
 ISO 527
8.70 GPa

@Temperature 80.0 °C
 1260 ksi

@Temperature 176 °F
 ISO 527
8.80 GPa

@Temperature 60.0 °C
 1280 ksi

@Temperature 140 °F
 ISO 527
9.00 GPa

@Temperature 120 °C
 1310 ksi

@Temperature 248 °F
 ISO 527
9.00 GPa

@Temperature 20.0 °C
 1310 ksi

@Temperature 68.0 °F
 ISO 527
Tensile Modulus 8.30 GPa
1200 ksi
Elasticity; ISO 527-1/-2
Fatigue Strength 45.0 MPa

@# of Cycles 1.00e+6
6530 psi

@# of Cycles 1.00e+6
55.0 MPa

@# of Cycles 100000
7980 psi

@# of Cycles 100000
69.0 MPa

@# of Cycles 10000
10000 psi

@# of Cycles 10000
Shear Modulus 0.0250 GPa

@Temperature 200 °C
 3.63 ksi

@Temperature 392 °F
 ISO 6721
0.800 GPa

@Temperature 175 °C
 116 ksi

@Temperature 347 °F
 ISO 6721
0.900 GPa

@Temperature 100 °C
 131 ksi

@Temperature 212 °F
 ISO 6721
0.950 GPa

@Temperature 50.0 °C
 138 ksi

@Temperature 122 °F
 ISO 6721
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180/A
7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/A
Izod Impact, Unnotched (ISO) 36.0 kJ/m²

@Temperature 120 °C
 17.1 ft-lb/in²

@Temperature 248 °F
 ISO 179/1eU
37.0 kJ/m²

@Temperature 70.0 °C
 17.6 ft-lb/in²

@Temperature 158 °F
 ISO 179/1eU
41.0 kJ/m²

@Temperature 25.0 °C
 19.5 ft-lb/in²

@Temperature 77.0 °F
 ISO 179/1eU
42.0 kJ/m²

@Temperature 0.000 °C
 20.0 ft-lb/in²

@Temperature 32.0 °F
 ISO 179/1eU
50.0 kJ/m²

@Temperature -25.0 °C
 23.8 ft-lb/in²

@Temperature -13.0 °F
 ISO 179/1eU
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179/1eU
4.00 J/cm²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU