SABIC Innovative Plastics LNP STAT-LOY N30009 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY N30009 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-loy* N30009 is a compound based on PC+ABS Blend resin containing Flame Retardant, Anti-Static. Added features of this material include: Antistat, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0053 - 0.0065 cm/cm @Time 86400 sec |
0.0053 - 0.0065 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0053 - 0.0065 cm/cm @Time 86400 sec |
0.0053 - 0.0065 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | ASTM D638 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.15 GPa | 312 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 2.15 GPa | 312 ksi | ASTM D790 |
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 38.0 J | 28.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Formosa Plastics Formolene® FORMAX® L91507H Film (Hexene Grade) LLDPE (discontinued **)
- Premix Premi-Glas® 1201-10 Polyester SMC (discontinued **)
- Multibase Multi-Flex® A 5001 E LC Black TPE Thermoplastic Elastomer
- Polyram PlusTek RA601 Nylon 6.6, Heat Resistant
- A. Schulman POLYBATCH™ Treated Pine 60181U/4 Concentrate Based In LLDPE
- 3A Composites Core Materials AIREX® R82.60 High Performance Structural Foam
- Bhansali Engineering Abstron SE-22 ABS Sheet Extrusion Grade
- Arkema Group Kynar® FLEX 2801 PVDF (discontinued **)
- Zircar Zirconia ZR-RIG Zirconia Rigidizer
- 3A Composites Core Materials AIREX® C70.75 Universal Structural Foam
Copyright © lookpolymers.com All Rights Reserved