SABIC Innovative Plastics LNP STAT-KON DEI13F PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DEI13F PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DEI13F is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 2% Silicone. Added features of this material include: Electrically Conductive, Superior Molding, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 116 MPa | 16800 psi | ASTM D638 |
| 116 MPa | 16800 psi | ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| 1.8 % | 1.8 % | ISO 527 | |
| Tensile Modulus | 10.1 GPa | 1460 ksi | 1 mm/min; ISO 527 |
| 10.4 GPa | 1510 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 167 MPa | 24200 psi | ISO 178 |
| 172 MPa | 24900 psi | ASTM D790 | |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| 9.79 GPa | 1420 ksi | ISO 178 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 25.0 J | 18.4 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 103 J | 76.0 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.24 | 0.24 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.24 | 0.24 | ASTM D3702 Modified |
| K (wear) Factor | 691 x 10-8 mm³/N-M | 343 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 9.00 µm/m-°C @Temperature -40.0 - 40.0 °C |
5.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 10.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
5.61 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 73.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 ohm-cm | 100 ohm-cm | ASTM D257 |
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Quadrant EPP Nylatron® GSM PA 6 + MoS2, cast (ISO Data)
- Techmer ES HiFill® PA6 GF33 L RD041 33% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP DX05475 PC
- ChevronTexaco Transformer Oil
- Arlon 51576B015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- BASF Polystyrol® 476 L Impact Grade Polystyrene (Europe)
- Arlon 99-108065 PTFE Resin
- E-Polymers EFLEX® S5040 Extrusion
- DuPont Elvax® 3128 Ethylene-Vinyl Acetate Copolymer Resin for Blown Film (discontinued **)
Copyright © lookpolymers.com All Rights Reserved