NOVA Chemicals Sclair® 2908, 2908-UV8A HDPE Injection Molding Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | NOVA Chemicals |
| Trade Name | Sclair® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 2908, 2908-UV8A HDPE Injection Molding Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: High stiffness, maximum impact strength and toughness.Applications: Tote boxes, beverage crates.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.961 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | <= 10 hour | <= 10 hour | F50, Condition A, ASTM D1693, 100% Igepal |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Break | 1200 % | 1200 % | ASTM D638 |
| Flexural Modulus | 1.28 GPa | 186 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 129 °C | 264 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 170 - 215 °C | 338 - 419 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LS3 PC
- NOVA Chemicals Sclair® 58G (High Gloss) HDPE Blow Molding Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 6-7833 Polyamide 12, with PTFE, lubricant modified
- I. Stern HIPS SH03 High Impact Polystyrene
- Industrial Laminates/Norplex MC507U Glass Fabric
- A. Schulman POLYFLAM™ RPP 1221 Low-Blooming, General Purpose Copolymer Polypropylene
- UBE UBESTA® 3030U Nylon 12 (After Toluene for 1000 hours)
- Akro-Plastic Akromid® T6 GF30 (3501) PPA Dry, 30% Glass Filled
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N774 Filler
- Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved