- Asahi Kasei Tenac®-C GN455 Copolymer Acetal Resin
Asahi Kasei Tenac®-C GN455 Copolymer Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | Asahi Kasei |
| Trade Name | Tenac®-C |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Tenac®-C GN455 Copolymer Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
25% Glass Fiber - filled, high-flow grade, with high stiffness and superior dimensional stabilityInformation provided by Asahi Kasei Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | Asahi Kasei Method |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | Asahi Kasei Method |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ISO 1133 D |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 - 1 & - 2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 - 1 & - 2 |
| Tensile Modulus | 8.30 GPa | 1200 ksi | ISO 527 - 1 & - 2 |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 / 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 -1 & -2 flat |
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | ISO 75 -1 & -2 flat |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8180 (479) (UF) Synthetic Oil
- SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Europe-Africa-Middle East)
- Nilit FRIANYL A63 HH-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced
- SABIC Innovative Plastics Lexan® OQ3820 PC (Asia Pacific)
- KB Alloys Ticar® 3% Ti - 0.3% C Titanium Carbon Aluminum Rod
- LG Chemical LUMID GP2200A(W) PA6+GF20%, General Purpose
- SABIC Innovative Plastics LNP STAT-KON AE008XXY ABS
- A. Schulman POLYBATCH™ White HS8350 Concentrate Based In Impact Polystyrene
- Chengdu Polyster H7560 Thermoplastic Polyether-ester Elastomer (TPEE)
- Unipetrol Heavy Stabilized Oil Hydrogenate
Copyright © lookpolymers.com All Rights Reserved