SABIC Innovative Plastics LNP STAT-KON DD000 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DD000 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DD000 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0084 cm/cm @Time 86400 sec |
0.0084 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0082 cm/cm @Time 86400 sec |
0.0082 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527 |
| 56.0 MPa | 8120 psi | ASTM D638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 |
| 62.0 MPa | 8990 psi | ASTM D638 | |
| Elongation at Break | 8.8 % | 8.8 % | ISO 527 |
| 9.5 % | 9.5 % | ASTM D638 | |
| Elongation at Yield | 4.4 % | 4.4 % | ISO 527 |
| 4.9 % | 4.9 % | ASTM D638 | |
| Tensile Modulus | 2.68 GPa | 389 ksi | 50 mm/min; ASTM D638 |
| 2.90 GPa | 421 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 102 MPa | 14800 psi | ASTM D790 |
| 102 MPa | 14800 psi | ISO 178 | |
| Flexural Modulus | 2.89 GPa | 419 ksi | ASTM D790 |
| 3.10 GPa | 450 ksi | ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.17 J/cm | 22.80 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 98.0 kJ/m² | 46.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Northstar Polymers PPA-059 Curing Agent
- NOVA Chemicals Surpass® FPs236-A Octene sMDPE Film Resin
- Global GA-3750 High Density Polyethylene, Film Extrusion Grade
- Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled
- Styrolution PS-168M Polystyrene
- United Cast Bar Unibar 600-3 Continuously Cast Spheroidal Graphite Iron
- Techmer Lehvoss Compounds Luvotech™ J-4/35 NAT PA6/12 (discontinued **)
- Ascend Performance Materials Vydyne® 22WSP Nylon 66, Weather Resistant, Conditioned
- DuPont Performance Polymers Zytel® 73G15L NC010 Nylon 6 (Unverified Data**)
- SABIC Innovative Plastics Lexan® 143R PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved