SABIC Innovative Plastics LNP Lubricomp RCP36XXP PA 66 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp RCP36XXP PA 66 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* RCP36XXP is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive, Easy Molding, Internally Lubricated.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
on tensile bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
5 mm/min; ISO 527
Elongation at Break 0.90 %
0.90 %
5 mm/min; ISO 527
Flexural Strength 236 MPa
34200 psi
2 mm/min; ISO 178
Flexural Modulus 12.0 GPa
1740 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 46.0 kJ/m²

@Temperature 23.0 °C
 21.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 244 °C
471 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af