SABIC Innovative Plastics LNP Lubricomp LL003E PEEK

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp LL003E PEEK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* LL003E is a compound based on Polyetheretherketone (PEEK) containing PTFE. Characteristics of this grade are: Easy Molding and Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D 792
Density 1.39 g/cc
0.0502 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.080 %
0.080 %
23°C / 50% RH; ISO 62
0.070 %

@Time 86400 sec
 0.070 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0090 - 0.020 cm/cm

@Time 86400 sec
 0.0090 - 0.020 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.0 MPa
8990 psi
5 mm/min; ISO 527
64.0 MPa
9280 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 62.0 MPa
8990 psi
5 mm/min; ISO 527
64.0 MPa
9280 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 3.3 %
3.3 %
5 mm/min; ISO 527
4.5 %
4.5 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 3.3 %
3.3 %
5 mm/min; ISO 527
4.5 %
4.5 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 3.00 GPa
435 ksi
50 mm/min; ASTM D 638
3.07 GPa
445 ksi
1 mm/min; ISO 527
Flexural Strength 92.0 MPa
13300 psi
ISO 178
Flexural Modulus 2.75 GPa
399 ksi
2 mm/min; ISO 178
2.94 GPa
426 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.480 J/cm

@Temperature 23.0 °C
 0.899 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 7.23 J/cm

@Temperature 23.0 °C
 13.5 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 37.0 kJ/m²

@Temperature 23.0 °C
 17.6 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 3.00 J

@Temperature 23.0 °C
 2.21 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.42
0.42
ASTM D 3702 Modified
Coefficient of Friction, Static 0.32
0.32
ASTM D 3702 Modified
K (wear) Factor 36.3 x 10-8 mm³/N-M
18.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 47.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 26.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 57.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 31.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 156 °C
313 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
156 °C

@Thickness 3.20 mm
 313 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 147 °C
297 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
146 °C

@Thickness 3.20 mm
 295 °F

@Thickness 0.126 in
 unannealed; ASTM D 648