SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* KL201 is a compound based on Acetal resin containing PTFE, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.970 % | 0.970 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.025 - 0.030 cm/cm @Time 86400 sec |
0.025 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.025 - 0.027 cm/cm @Time 86400 sec |
0.025 - 0.027 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| 53.0 MPa | 7690 psi | ISO 527 | |
| Elongation at Yield | 20 % | 20 % | ASTM D638 |
| Tensile Modulus | 2.65 GPa | 384 ksi | 50 mm/min; ASTM D638 |
| 3.05 GPa | 442 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | ASTM D790 |
| 2.26 GPa | 328 ksi | ISO 178 | |
| Izod Impact, Notched | 0.680 J/cm | 1.27 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.67 J/cm | 25.61 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.090 | 0.090 | ASTM D3702 Modified |
| K (wear) Factor | 24.2 x 10-8 mm³/N-M | 12.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 88.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 85.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GTP09005 PVC
- Resin Technology Group Fusion 513 Rubber and Plastic Bonding Fusion Cyanoacrylate
- Advanced Elastomer Systems Santoprene® 8281-90 Thermoplastic Rubber (discontinued **)
- Solvay Specialty Polymers Hylar® 301F Polyvinylidene Fluoride (PVDF) (Unverified Data**)
- 3M Dyneon™ CC605 PTFE 25% Fiberglass Filled (discontinued **)
- LG Chemical Lupox® PBT-LW5303 30% Glass Filled Low Warp PBT
- Lubrizol Estane® 2355-55DE Thermoplastic Polyurethane
- BASF Ultramid® A27 E 01 PA66 (Conditioned)
- Ascend Performance Materials Vydyne® 41H BK03 Nylon 66, Impact Modified, DAM
- Lehmann & Voss LUVOCOM® 1-7003 Polyamide 66, with carbon fiber and PTFE, heat stabilized
Copyright © lookpolymers.com All Rights Reserved