Lubrizol Estane® 2102-55D Thermoplastic Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Estane® 2102-55D Thermoplastic Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formerly PellethaneFeature: Load-bearing capacityAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by Lubrizol.Lubrizol acquired the Pellethane product line from Dow in 2009.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
ASTM D955
Melt Flow 14 g/10 min

@Load 2.16 kg,
Temperature 224 °C
14 g/10 min

@Load 4.76 lb,
Temperature 435 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 58
58
ASTM D2240
Tensile Strength, Ultimate 49.5 MPa
7180 psi
ASTM D412
Elongation at Break 415 %
415 %
ASTM D412
50% Modulus 0.0153 GPa
2.22 ksi
ASTM D412
100% Modulus 0.0162 GPa
2.35 ksi
ASTM D412
300% Modulus 0.0359 GPa
5.21 ksi
ASTM D412
Flexural Modulus 0.172 GPa
24.9 ksi
ASTM D790
Tear Strength 179 kN/m
1020 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 60
60
H22 Wheel, 1000g; ASTM D1044
Compression Set 25 %

@Temperature 25.0 °C,
Time 79200 sec
25 %

@Temperature 77.0 °F,
Time 22.0 hour
ASTM D395, Method B
27 %

@Temperature 70.0 °C,
Time 79200 sec
27 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D395, Method B
Tensile Set 30 %
30 %
Elongation set after break; ASTM D412
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 135 µm/m-°C

@Temperature 20.0 °C
75.0 µin/in-°F

@Temperature 68.0 °F
ASTM D636
Vicat Softening Point 118 °C
244 °F
120°C/hr, 9.8N; ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 204 - 221 °C
399 - 430 °F
Molding
Mold Temperature 16.0 - 60.0 °C
60.8 - 140 °F
Drying Temperature 88.0 - 104 °C
190 - 219 °F
air dew point <-40°C