SABIC Innovative Plastics LNP THERMOCOMP PF008S PA 6 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PF008S PA 6 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* PF008S is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.980 % | 0.980 % | 50% RH, 24 hrs; ASTM D570 |
| 1.26 % | 1.26 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 183 MPa | 26500 psi | ASTM D638 |
| 186 MPa | 27000 psi | ISO 527 | |
| Elongation at Break | 3.3 % | 3.3 % | ISO 527 |
| 3.3 % | 3.3 % | ASTM D638 | |
| Tensile Modulus | 12.67 GPa | 1838 ksi | 50 mm/min; ASTM D638 |
| 12.99 GPa | 1884 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 278 MPa | 40300 psi | ISO 178 |
| 278 MPa | 40300 psi | ASTM D790 | |
| Flexural Modulus | 9.25 GPa | 1340 ksi | ASTM D790 |
| 9.53 GPa | 1380 ksi | ISO 178 | |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 92.0 kJ/m² | 43.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 25.0 J | 18.4 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 21.0 J | 15.5 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® D6975CT TPE, Extruded
- SABIC Innovative Plastics Cycolac® G360 ABS (Europe-Africa-Middle East)
- Saint-Gobain CHR® M823 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- A. Schulman ComAlloy® E-13086 Glass/TFE Reinforced PPS
- ExxonMobil EXACT™ 4150 Plastomer
- ExxonMobil Jayflex™ DINP Plasticizer
- DuPont Teijin Films Melinex® S Polyester Film, 200 Gauge
- Abatron Abosolv™ General Purpose Thinner and Solvent
- 3M Scotch-Weld™ TE230 Black Polyurethane Reactive Adhesive
- Latrobe Dynamax™ ASTM M42, DIN 1.3247 Super High Speed Steel
Copyright © lookpolymers.com All Rights Reserved