SABIC Innovative Plastics LNP LUBRICOMP UFL36SXP PPA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP UFL36SXP PPA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* UFL36SXP is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 187 MPa | 27100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 10.4 GPa | 1510 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 239 MPa | 34700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.90 GPa | 1290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1105-8179 PEEK, with carbon fiber
- Teknor Apex APEX® 4103 Polyvinyl Chloride, Flexible
- Solvay GEROPON® HW 15 N Surfactant
- SABIC Innovative Plastics NORYL PX500 PPE (Asia Pacific)
- ELM® SoyGrease™ EP Plus Biodegradable Extreme Pressure Grease, NLGI Grade 3
- Arlon LW50125R##-P1 0.050" (1.27 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- 3M Dyneon™ PVDF 6108/0001 Polyvinylidene Fluoride
- Akro-Plastic Akromid® B3 GF 30 S1 NAT. (1383) PA, Cold-Impact Resistant, 30% Glass Filled, Natural
- Overview of materials for Acrylic/Polycarbonate Alloy, Carbon Fiber Filler
- Arlon 55279R031 0.031" (0.787 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved