| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RP004 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RP004 is a compound based on Nylon 66 resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.840 % | 0.840 % | 50% RH, 24 hrs; ASTM D570 |
| 1.10 % | 1.10 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
| 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
| 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 22.6 % | 22.6 % | Type I, 5 mm/min; ASTM D638 |
| 26.6 % | 26.6 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 22 % | 22 % | Type I, 5 mm/min; ASTM D638 |
| 26 % | 26 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.61 GPa | 379 ksi | 50 mm/min; ASTM D638 |
| 2.72 GPa | 395 ksi | 1 mm/min; ISO 527 | |
| Flexural Modulus | 2.26 GPa | 328 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.39 GPa | 347 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.48 J/cm | 6.52 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 88.0 kJ/m² | 41.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.010 | 0.010 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.040 | 0.040 | ASTM D3702 Modified |
| K (wear) Factor | 6.04 x 10-8 mm³/N-M | 3.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 94.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
52.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 237 °C @Thickness 3.20 mm |
459 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 64.0 °C @Thickness 3.20 mm |
147 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 7011 C Natural 70% Filler Content Polypropylene
- Rotuba 860MS 686.5 Ethyl Cellulose
- SABIC Innovative Plastics LNP Thermocomp OF004AER PPS
- Star Plastics ABS3545 Molding Grade ABS
- ExxonMobil Exxsol™ D30 Dearomatized Fluid
- 3M Scotch® 605 Transparent Film Tape
- 3M Scotchcal™ 1000-41 Graphic Film
- Ceradyne Thermo-Sil® HS Fused Silica
- 3M Scotchcal™ ElectroCut™ 7725-47 Graphic Film
- Aremco Corr-Paint™ CP4000-S High Temperature Protective Coating Silicone-Polyester