Solvay Specialty Polymers Supradel® HTS-2630 High Temperature Sulfone Resin  (discontinued **)

Category Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Supradel® HTS-2630 High Temperature Sulfone Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SUPRADEL HTS-2630 is a 30% glass-fiber reinforced high-temperature, high-performance, amorphous, sulfone polymer.In addition to exceptional thermal performance, this resin has the other performance features and attributes traditionally known for sulfone polymers. These features include good strength, stiffness, and dielectric properties over a wide temperature range, resistance to hydrolysis by hot water and steam environments, excellent resistance to acids and bases, and inherent flammability resistance. The resin also offers a high degree of dimensional control during fabrication and dimensional stability during part service life.SUPRADEL HTS-2630 resin is easily amenable to fabrication by injection molding, and other thermoplastic fabrication techniques. By virtue of its very high temperature performance and the unique combination of other engineering attributes, SUPRADEL HTS-2630 resin constitutes a good candidate for metal replacement as well as non-thermoplastic resin replacement in a wide range of engineering applications. SUPRADEL HTS-2630 resin is available in natural and black.Information provided by Solvay Advanced Polymers
Physical Properties Metric English Comments
Specific Gravity 1.55 g/cc
1.55 g/cc
ASTM D792
Water Absorption 0.40 %
0.40 %
At 24 hours; ASTM D570
Water Absorption at Saturation 1.5 %
1.5 %
ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM D955
Melt Flow 5.5 g/10 min

@Load 5.00 kg,
Temperature 400 °C
5.5 g/10 min

@Load 11.0 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 112 MPa
16300 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Tensile Modulus 8.96 GPa
1300 ksi
ASTM D638
Flexural Strength 164 MPa
23800 psi
ASTM D790
Flexural Modulus 7.58 GPa
1100 ksi
ASTM D790
Izod Impact, Notched 0.641 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.34 J/cm
10.0 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
Annealed 0.125 inch thick specimen; ASTM D648
Glass Transition Temp, Tg 265 °C
509 °F
Processing Properties Metric English Comments
Melt Temperature 390 - 410 °C
734 - 770 °F
Stock Temperature
Mold Temperature >= 180 °C
>= 356 °F
190 - 210 °C
374 - 410 °F
Long flow or thin wall parts or for low residual stress
Drying Temperature 150 °C
302 °F
2.5 hours for injection molding
170 °C
338 °F
> 4 hours hopper drying with desiccated air inlet for extrusion