SABIC Innovative Plastics LNP LUBRICOMP RP002 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RP002 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RP002 is a compound based on PA 66 resin containing PTFE, Silicone: Added features include; Internallly Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 67.0 MPa | 9720 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 17.1 % | 17.1 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 7.9 % | 7.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.80 GPa | 406 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Oceanchem Group Melamine Cyanurate (MCA)
- I. Stern WC-102 General Purpose Crystal Polystyrene
- Techmer ES HiFill® PA6/6 GF33 BK024 33% Glass Filled (Conditioned)
- A. Schulman POLYFLAM™ CFP 4611 11% CACO3 filled copolymer polypropylene product
- Ensinger Tecatron® XP-79 Compression Molded PPS Compound, 70% PTFE Filled Seal Material
- Carlson Nitronic® 50® Austenitic Stainless Steel
- Asahi Kasei Xyron® A0210 PPE/PA
- Asahi Kasei Xyron® 220V Modified Polyphenylene Ether
- Braskem H 501HC Thermoforming Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved