BASF Ultradur S 4090 G4 BK5110 20% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultradur S
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur S 4090 G4 BK5110 20% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultradur S 4090 G4 BK5110 is a 20% glass reinforced, pigmented black PBT+ASA blend. It produces moldings with good surface finish,is resistant to chemicals and stress cracking, and has low shrinkage and warpage.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 98.0 MPa
14200 psi
5mm/min; ISO 527
Elongation at Break 2.8 %
2.8 %
5mm/min; ISO 527
Tensile Modulus 6.33 GPa
918 ksi
1mm/min; ISO 527
Flexural Modulus 5.91 GPa
857 ksi
ISO Data
Izod Impact, Notched (ISO) 6.40 kJ/m²
3.05 ft-lb/in²
ISO Test
Charpy Impact, Notched 0.640 J/cm²
3.05 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 223 °C
433 °F
10 K/min
223 °C
433 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 208 °C
406 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 168 °C
334 °F
ISO 75
Descriptive Properties Value Comments
Color BK5110
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding
Special characteristic Heat stabilized or stable to heat
Light stabilized or stable to light
Lubricant
U.V. stabilized or stable to weather