SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* RFL36S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 159 MPa | 23100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.1 % | 3.1 % | 5 mm/min; ISO 527 |
| Flexural Strength | 235 MPa | 34100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² | 38.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
12.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 60.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 220 °C | >= 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 220 °C | >= 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- MV Labs CA200 CaBr2·xH2O Calcium bromide hydrate
- Ravago Manufacturing Americas Hylex® P1310L Polycarbonate, UV Stabilized, Intermediate Flow, Mold Release
- Polymer Resources AC-GP3 Acetal Copolymer, High Flow, Thin Wall Applications
- Cookson Group Plaskon® S-7LA Molding Compound (discontinued **)
- Stratasys® Polycarbonate
- SABIC Innovative Plastics LNP Stat-loy W3000 PBT
- Wellman Wellamid® FR1841-BK1 Nylon 66, Unfilled, Flame Retardant
- ExxonMobil LLDPE LLP 8460.29 Linear Low Density Polyethylene Resin
- BP Amoco Acctuf® 3240 Impact Copolymer Polypropylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved