PolyOne Edgetek® NN-40CF/000 FRV0 NATURAL Polyamide 66 (Nylon 66)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	PolyOne Corporation
Trade Name	Edgetek®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Edgetek® NN-40CF/000 FRV0 NATURAL Polyamide 66 (Nylon 66).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.52 g/cc	1.52 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.020 - 0.040 cm/cm @Thickness 3.18 mm	0.020 - 0.040 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	221 MPa	32100 psi	5.1 mm/min; ASTM D638
Elongation at Break	1.0 %	1.0 %	5.1 mm/min; ASTM D638
Tensile Modulus	37.9 GPa	5500 ksi	5.1 mm/min; ASTM D638
Flexural Strength	331 MPa	48000 psi	1.3 mm/min; ASTM D790
Flexural Modulus	26.2 GPa	3800 ksi	1.3 mm/min; ASTM D790
Izod Impact, Notched	0.680 J/cm	1.27 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	245 °C @Thickness 3.18 mm	473 °F @Thickness 0.125 in	Unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	100 - 10000 ohm-cm	100 - 10000 ohm-cm	ASTM D257
Surface Resistance	100 - 10000 ohm	100 - 10000 ohm	ASTM D257

Descriptive Properties	Value	Comments
Features	Flame Retardant
	High Stiffness
	Semi Crystalline
Filler / Reinforcement	Carbon Fiber Reinforcement, 40% Filler by Weight
Forms	Pellets
Generic Material	Nylon 66
Generic Name	Polyamide 66 (Nylon 66)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Aerospace Applications
	Automotive Electronics
	Business Equipment
	Computer Components
	Connectors
	Consumer Applications
	Electrical Housing
	Electrical/Electronic Applications
	Structural Parts